Some properties of YBamCu1+mOy (m = 2,3,4,5) superconductors
Piyamas Chainok, Thanarat Khuntak, Supphadate Sujinnapram, Somporn Tiyasri, Wirat Wongphakdee, Thitipong Kruaehong, Tunyanop Nilkamjon, Sermsuk Ratreng, Pongkaew Udomsamuthirun
arXiv:1503.08515 · DOI 10.1142/S0217979215500605 · 2015-03-30 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We synthesized the YBamCu1+mOy superconductors; m = 2,3,4,5 that were Y123 (YBa2Cu3O7-x), Y134 (YBa3Cu4O9-x), Y145 (YBa4Cu5O11-x), Y156 (YBa5Cu6O13-x), by solid state reaction with the Y2O3, BaCO3 and CuO as the beginning materials. The calcination temperature was 950 C and varied the sintering temperature to be 950 C and 980 C. The resistivity measurement by four-point-probe technique showed that the Tconset of Y123, Y134, Y145, Y156 were at 97 K, 93 K, 91K, 85 K, respectively. The XRD and Rietveld full-profile analysis method were used and found that the crystal structure was in the orthorhombic with Pmmm space group with the ratio c/a were 3.0, 4.0, 5.0 and 6.0 for Y123, Y134, Y145 and Y156, respectively. The oxygen content was characterized by Iodometric titration. The (Cu3+/Cu2+and Oxygen content) were (0.28, 6.83), (0.19, 8.81), (0.13, 10.79), (0.16, 12.92) of Y123, Y134, Y145, Y156 respectively. We also found that the increasing of sintering temperature has reduced the oxygen content and the critical temperature of all samples.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| YBa2Cu3O7-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 97 | Pressure not reported | onset |
| YBa3Cu4O9-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 93 | Pressure not reported | onset |
| YBa4Cu5O11-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 91 | Pressure not reported | onset |
| YBa5Cu6O13-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 85 | Pressure not reported | onset |
Similar papers
Superconductivity at 90 K in a multiphase oxide of Y-Ba-Cu
similarity 0.88J. M. Tarascon et al.
Source status unknown — claims are unverified
Effect of compositional variation and annealing in oxygen on superconducting properties of Y1Ba2Cu3O8−y
similarity 0.87A. J. Panson et al.
Source status unknown — claims are unverified
Fabrication of Superconducting YBa2Cu4O8 Film via Coprecipitation
similarity 0.87Hiroshi Hara et al. · 2019 · arXiv:1904.03506
Source status unknown — claims are unverified
Fe57 Mössbauer study of the superconductor YBa2(FexCu1−x)3Oy
similarity 0.87E. Baggio-Saitovitch et al.
Source status unknown — claims are unverified
Oxygen content and superconductivity in Y0.8Ca0.2Ba2Cu3Oy (y=6.03–6.89)
similarity 0.87J. Hejtmánek et al.
Source status unknown — claims are unverified
Broader perspective on the high-temperature superconducting YBa2Cu3Oy system: The real role of the oxygen content
similarity 0.87Y. Tokura et al.
Source status unknown — claims are unverified