Localized High Frequency Electrodynamic Behavior of Optimally-doped Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ Single Crystal films

Tamin Tai; Behnood G. Ghamsari; J. H. Kang; S. Lee; C. B. Eom; Steven M. Anlage

Localized High Frequency Electrodynamic Behavior of Optimally-doped Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ Single Crystal films

Tamin Tai, Behnood G. Ghamsari, J. H. Kang, S. Lee, C. B. Eom, Steven M. Anlage

arXiv:1507.03318 · 2015-07-13

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Localized high frequency (several GHz) electrodynamic properties of a high quality epitaxial, single-crystal Iron-Pnicitde Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ thin film near optimal doping (x=0.08) are measured under a localized and strong RF magnetic field, created by a near-field microwave microscope. Two reflection electrodynamic measurements, including linear and the third harmonic responses, are performed to understand the electromagnetic properties of Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$. Our measurement results show that Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ has have a wide superconducting transition width and may have a multi-gap nature. In addition, based on the $1/T^2$ dependence of the third harmonics signal at lower temperature, Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ shows the possibility of nodal behavior.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Ba(Fe0.92Co0.08)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	18.1	Pressure not reported	zero_resistance
Nb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.3	Pressure not reported	unknown