Fragile structural transition in Mo3Sb7

J. -Q. Yan; M. A. McGuire; A. F. May; D. Parker; D. G. Mandrus; B. C. Sales

Fragile structural transition in Mo3Sb7

J. -Q. Yan, M. A. McGuire, A. F. May, D. Parker, D. G. Mandrus, B. C. Sales

arXiv:1507.06192 · 2015-07-22

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Mo$_3$Sb$_7$ single crystals lightly doped with Cr, Ru, or Te are studied in order to explore the interplay between superconductivity, magnetism, and the cubic-tetragonal structural transition. The structural transition at 53\,K is extremely sensitive to Ru or Te substitution which introduce additional electrons, but robust against Cr substitution. No sign of a structure transition was observed in superconducting Mo$_{2.91}$Ru$_{0.09}$Sb$_7$ and Mo$_3$Sb$_{6.975}$Te$_{0.025}$. In contrast, 3at\% Cr doping only slightly suppresses the structural transition to 48\,K while leaving no trace of superconductivity above 1.8\,K. Analysis of magnetic properties suggests that the interdimer interaction in Mo$_3$Sb$_7$ is near a critical value and essential for the structural transition. All dopants suppress the superconductivity of Mo$_3$Sb$_7$. The tetragonal structure is not necessary for superconductivity.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Mo3Sb7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.35	Pressure not reported	unknown
Mo3Sb7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.35	Pressure not reported	unknown
Mo3Sb7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.35	Pressure not reported	unknown
Mo2.91Ru0.09Sb7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.15	Pressure not reported	unknown
Mo2.91Ru0.09Sb7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.15	Pressure not reported	unknown
Mo2.91Ru0.09Sb7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.15	Pressure not reported	unknown
Mo3Sb6.975Te0.025 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.05	Pressure not reported	unknown
Mo3Sb6.975Te0.025 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.05	Pressure not reported	unknown
Mo3Sb6.975Te0.025 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.05	Pressure not reported	unknown
Mo3Sb7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.08	Pressure not reported	unknown