Superconductivity in the Niobium-rich compound Nb5Se4
T. Klimczuk, K. Baroudi, J. W. Krizan, A. L. Kozub, R. J. Cava
arXiv:1512.04144 · DOI 10.1002/CHIN.201546004 · 2015-12-14 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The niobium rich selenide compound Nb5Se4 was synthesized at ambient pressure by high-temperature solid-state reaction in a sealed Ta tube. Resistivity and heat capacity measurements reveal that this compound is superconducting, with a T_c = 1.85K. The electronic contribution to the specific heat γ and the Debye temperature are found to be 18.1 mJ/mol/K^2 and 298 K respectively. The calculated electron-phonon coupling constant λ_ep = 0.5 and the ΔC_p/γTc = 1.42 ratio imply that Nb5Se4 is a weak coupling BCS superconductor. The upper critical field and coherence length are found to be 1.44 T and 15.1 nm, respectively.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Nb5Se4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 1.85 | Pressure unresolved | unknown |
| Nb5Se4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 1.85 | Pressure unresolved | unknown |
Similar papers
Robust superconductivity with large upper critical field in Nb2PdS5
similarity 0.89Rajveer Jha et al. · 2013 · arXiv:1312.0425
Source status unknown — claims are unverified
Superconductivity at 5.5 K in Nb2PdSe5 compound
similarity 0.88Reena Goyal et al. · 2016 · arXiv:1606.09369
Source status unknown — claims are unverified
Specific heat of robust Nb2PdS5 superconductor
similarity 0.88Reena Goyal et al. · 2014 · arXiv:1412.4890
Source status unknown — claims are unverified
Structure- and composition-tunable superconductivity, band topology, and elastic response of hard binary niobium nitrides Nb2N, Nb4N3 and Nb4N5
similarity 0.87K. Ramesh Babu & Guang-Yu Guo
Source status unknown — claims are unverified
Nodeless two-gap superconductivity revealed by low-temperature specific heat and lower critical field in 4Ha−NbSe2
similarity 0.87Menghu Zhou et al.
Source status unknown — claims are unverified
Superconducting properties and electronic structure of NaBi
similarity 0.87S K Kushwaha et al. · 2014 · arXiv:1403.3869
Source status unknown — claims are unverified