Superconductivity at 3.85 K in BaPd2As2 with the ThCr2Si2-type structure

Qi Guo; Jia Yu; Bin-Bin Ruan; Dong-Yun Chen; Xiao-Chuan Wang; Qing-Ge Mu; Bo-Jin Pan; Gen-Fu Chen; Zhi-An Ren

doi:10.1209/0295-5075/113/17002

← Back to search

Superconductivity at 3.85 K in BaPd2As2 with the ThCr2Si2-type structure

Qi Guo, Jia Yu, Bin-Bin Ruan, Dong-Yun Chen, Xiao-Chuan Wang, Qing-Ge Mu, Bo-Jin Pan, Gen-Fu Chen, Zhi-An Ren

arXiv:1512.06340 · DOI 10.1209/0295-5075/113/17002 · 2015-12-20 · Europhysics Letters

T1experimental20 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The single crystal of ThCr2Si2-type BaPd2As2 was successfully prepared by a self-flux method, and the crystal structure was characterized by X-ray diffraction method with the lattice parameters a = 4.489(2) Å and c = 10.322(3) Å. Bulk superconductivity below a Tc (critical temperature) of 3.85 K was revealed in this compound by the measurements of resistivity, magnetic susceptibility and specific heat, and this Tc is much higher than those of other isostructural Pd-based superconductors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
BaPd2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.85	Pressure not reported	unknown
BaPd2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.85	Pressure not reported	unknown
BaPd2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.85	Pressure not reported	unknown