Rattling enhanced superconductivity in MV$_2$Al$_{20}$ (M = Sc, Lu, Y) intermetallic cage compounds

Michał J. Winiarski; Bartłomiej Wiendlocha; Małgorzata Sternik; Piotr Wiśniewski; James R. O'Brien; Dariusz Kaczorowski; Tomasz Klimczuk

doi:10.1103/PhysRevB.93.134507

Rattling enhanced superconductivity in MV$_2$Al$_{20}$ (M = Sc, Lu, Y) intermetallic cage compounds

Michał J. Winiarski, Bartłomiej Wiendlocha, Małgorzata Sternik, Piotr Wiśniewski, James R. O'Brien, Dariusz Kaczorowski, Tomasz Klimczuk

arXiv:1603.05320 · DOI 10.1103/PhysRevB.93.134507 · 2016-03-17 · Physical Review B

T1experimental31 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Polycrystalline samples of four intermetallic compounds: MV$_2$Al$_{20}$ (M = Sc, Y, La, and Lu) were synthesized using an arc-melting technique. The crystal structures were analyzed by means of powder x-ray diffraction and Rietveld analysis, and the physical properties were studied by means of heat capacity, electrical resistivity and magnetic susceptibility measurements down to 0.4 K. For ScV$_2$Al$_{20}$, LuV$_2$Al$_{20}$, and YV$_2$Al$_{20}$, superconductivity was observed with critical temperatures T$_c$ = 1.00 K, 0.57 K, and 0.60 K, respectively. Superconductivity for the Lu compound is reported for the first time. Theoretical calculations of the electronic and phonon structures were conducted in order to analyze the superconductivity and dynamics in ScV$_2$Al$_{20}$, YV$_2$Al$_{20}$, and LuV$_2$Al$_{20}$ and to explain the lack of a superconducting transition in LaV$_2$Al$_{20}$ down to 0.4 K. The results of the experimental and theoretical studies show that all the compounds are weakly-coupled type II BCS superconductors, and reveal the importance of the M-atom anharmonic "rattling" modes for the superconductivity in these materials, which seem to enhance T$_c$, especially for ScV$_2$Al$_{20}$.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
ScV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1	Pressure not reported	unknown
ScV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1	Pressure not reported	unknown
ScV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1	Pressure not reported	unknown
LuV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.57	Pressure not reported	unknown
LuV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.57	Pressure not reported	unknown
LuV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.57	Pressure not reported	unknown
YV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.6	Pressure not reported	unknown
YV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.6	Pressure not reported	unknown
YV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.6	Pressure not reported	unknown