Crystal structure instability of FeSe grains: Formation of non-superconducting phase at the grain surface
Hiroki Izawa, Yuji Tanaka, Yoshikazu Mizuguchi, Osuke Miura
arXiv:1604.00709 · DOI 10.7567/JJAP.55.053101 · 2016-04-04 · Japanese Journal of Applied Physics
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We investigated the magnetization and crystal structure of FeSe polycrystalline samples with various grain sizes. For the samples with large grains, a large magnetic critical current density Jc was observed. For the samples with small grains, superconductivity signals were not observed; instead, magnetization hysteresis, which is not a result of superconductivity, was observed. In the X-ray diffraction pattern for the samples with small grains, broad additional peaks were observed, corresponding to the formation of the non-superconducting (monoclinic) Fe-Se phase at the FeSe grain surface. The crystal structure instability at the grain surface would be the reason for the low superconducting properties of the Fe-chalcogenide polycrystalline wires investigated thus far.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Disorder-driven electronic localization and phase separation in superconducting Fe1+yTe0.5Se0.5 single crystals
similarity 0.89S. Rößler et al.
Source status unknown — claims are unverified
The Structural Phase Transition in FeSe (Fe1+dSe)
similarity 0.88T. M. McQueen et al. · 2009 · arXiv:0905.1065
Source status unknown — claims are unverified
Electronic and Superconducting Properties of Some FeSe-based Single Crystals and Films Grown Hydrothermally
similarity 0.88Xiaoli Dong et al. · 2020 · arXiv:2009.05731
Source status unknown — claims are unverified
Electric Transport of a Single Crystal Iron Chalcogenide FeSe Superconductor: Evidence of Symmetry Breakdown Nematicity and Additional Ultrafast Dirac cone-Like Carriers
similarity 0.88K. K. Huynh et al. · 2014 · arXiv:1405.3815
Source status unknown — claims are unverified
Synthesis, crystal structure, and chemical stability of the superconductor FeSe1−x
similarity 0.88E. Pomjakushina et al.
Source status unknown — claims are unverified
Disorder-robust high-field superconducting phase of FeSe single crystals
similarity 0.88Nan Zhou et al. · 2021 · arXiv:2102.02353
Source status unknown — claims are unverified