New Superconducting Phase of Li$_x$(C$_6$H$_{16}$N$_2$)$_y$Fe$_{2-z}$Se$_2$ with $T_\textrm{c}$ = 41 K Obtained through the Post-Annealing
Shohei Hosono, Takashi Noji, Takehiro Hatakeda, Takayuki Kawamata, Masatsune Kato, Yoji Koike
arXiv:1604.03262 · DOI 10.7566/JPSJ.85.013702 · 2016-04-12 · Journal of the Physical Society of Japan
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Post-annealing effects on the crystal structure and superconductivity of the lithium- and hexamethylenediamine (HMDA)-intercalated superconductor Lix(C6H16N2)yFe2-zSe2 have been investigated. Through the post-annealing, a two-step reduction of the interlayer spacing between neighboring Fe layers, d, has been observed. It has been found that a new phase of Lix(C6H16N2)yFe2-zSe2 with d= 10.30(2) Å and Tc = 41 K different from the as-intercalated phase is stabilized owing to the possible stable inclination of HMDA intercalated between FeSe layers. This result supports the domic relation between Tc and d in the FeSe-based intercalation superconductors. The reason why Tc increases with a decrease in d through the post-annealing is discussed.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Lix(C6H16N2)yFe2-zSe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 41 | Pressure not reported | unknown |
Similar papers
Superconductivity and Intercalation Statein the Lithium-Hexamethylenediamine-Intercalated Superconductor Li(CHN)FeSe: Dependence on the Intercalation Temperature and Lithium Content
similarity 0.92Shohei Hosono et al. · 2016 · arXiv:1607.05873
Source status unknown — claims are unverified
New intercalation superconductor Lix(C6H16N2)yFe2-zSe2 with a very large interlayer-spacing and Tc = 38 K
similarity 0.91S. Hosono et al. · 2015 · arXiv:1510.08625
Source status unknown — claims are unverified
New Li-Ethylenediamine-Intercalated Superconductor Li(CHN)FeSe with = 45 K
similarity 0.90Takehiro Hatakeda et al. · 2013 · arXiv:1311.0141
Source status unknown — claims are unverified
New Alkali-Metal- and 2-Phenethylamine-Intercalated Superconductors (CHN)FeSe ( = Li, Na) with the Largest Interlayer Spacings and 40 K
similarity 0.89Takehiro Hatakeda et al. · 2016 · arXiv:1609.06017
Source status unknown — claims are unverified
Synthesis of New Lithium- and Monoamine-Intercalated Superconductors Li(CHN)FeSe ( = 6, 8, 18) with the Dramatically Expanded Interlayer Spacing
similarity 0.89Chika Sakamoto et al. · 2020 · arXiv:2012.08145
Source status unknown — claims are unverified
Emergence of magnetism and controlling factors of superconductivity in Li/Na-ammonia cointercalated FeSe1−zTez
similarity 0.88Hechang Lei (雷和畅) et al.
Source status unknown — claims are unverified