Growth and characterization of CaFe$_{1-x}$Co$_x$AsF single crystals by CaAs flux method
Yonghui Ma, Kangkang Hu, Qiucheng Ji, Bo Gao, Hui Zhang, Gang Mu, Fuqiang Huang, Xiaoming Xie
arXiv:1605.04642 · DOI 10.1016/j.jcrysgro.2016.07.029 · 2016-05-16 · Journal of Crystal Growth
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Millimeter sized single crystals of CaFe$_{1-x}$Co$_x$AsF were grown using a self-flux method. It is found that high-quality single crystals can be grown from three approaches with different initial raw materials. The chemical compositions and crystal structure were characterized carefully. The c-axis lattice constant is suppressed by the Co substitution. Superconductivity with the critical transition $T_c$ as high as 21 K was confirmed by both the resistivity and magnetic susceptibility measurements in the sample with $x$ = 0.12. Moreover, it is found that $T_c$ can be enhanced for about 1 K under the very small hydrostatic pressure of 0.22 GPa, which is more quickly than that reported in the polycrystalline samples. Our results is a promotion for the physical investigations of 1111 phase iron-pnictide superconductors.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| CaFe0.88Co0.12AsF Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 22 | Pressure unresolved | onset |
| CaFe0.88Co0.12AsF Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 20 | Pressure unresolved | zero_resistance |
| CaFe0.88Co0.12AsF Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 21 | Pressure unresolved | unknown |
| CaFe0.88Co0.12AsF Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 22 | 0.22 GPa | unknown |
Similar papers
Two-Gap Superconductivity in CaFe_{0.88}Co_{0.12}AsF Revealed by Temperature Dependence of the Lower Critical Field H_{c1}^c(T)
similarity 0.91Teng Wang et al. · 2019 · arXiv:1907.04033
Source status unknown — claims are unverified
Growth and Characterization of Millimeter-sized Single Crystals of CaFeAsF
similarity 0.91Yonghui Ma et al. · 2015 · arXiv:1505.06014
Source status unknown — claims are unverified
The effect of As-Chain layers in CaFeAs
similarity 0.90Xianxin Wu et al. · 2014 · arXiv:1402.4712
Source status unknown — claims are unverified
Effect of pressure on transport and magnetotransport properties in CaFe2As2 single crystals
similarity 0.90M. S. Torikachvili et al. · 2009 · arXiv:0905.4002
Source status unknown — claims are unverified
Superconductivity at 33 K in "111" single crystals at ambient pressure
similarity 0.90T. -L. Xia et al. · 2010 · arXiv:1001.3311
Source status unknown — claims are unverified
Pressure Effects on the Superconducting and Spin-Density-Wave States of the Newly Discovered Sm(O1-xFx)FeAs
similarity 0.90B. Lorenz et al. · 2008 · arXiv:0804.1582
Source status unknown — claims are unverified