Flux free growth of superconducting FeSe single crystals
P. K. Maheshwari, L. M. Joshi, Bhasker Gahtori, A. K. Srivastava, Anurag Gupta, S. P. Patnaik, V. P. S. Awana
arXiv:1606.08201 · DOI 10.1088/2053-1591/3/7/076002 · 2016-06-27 · Materials Research Express
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report flux free growth of superconducting FeSe single crystals by an easy and versatile high temperature melt and slow cooling method for first time. The room temperature XRD on the surface of the piece of such obtained crystals showed single 101 plane of Beta-FeSe tetragonal phase. The bulk powder XRD, being obtained by crushing the part of crystal chunk showed majority tetragonal and minority FeSe hexagonal crystalline phases. Detailed HRTEM images along with SAED (selected area electron diffraction) showed the abundance of both majority and minority FeSe phases. Both transport (RT) and magnetization (MT) exhibited superconductivity at below around 10K. Interestingly, the magnetization signal of these crystals is dominated by the magnetism of minority magnetic phase, and hence the isothermal magnetization (MH) at 4K was seen to be ferromagnetic (FM) like. Transport (R-T) measurements under magnetic field showed superconductivity onset at below 12K, and R = 0 (Tc) at 9K. Superconducting transition temperature (Tc) decreases with applied field to around 6K at 7Tesla, with dTc/dH of 0.4K/Tesla, giving rise to an Hc2 value of around 50 Tesla, 30 Tesla and 20 Tesla for Rn = 90, 50 and 10 percent respectively. FeSe single crystal activation energy is calculated from Thermally Activated Flux Flow (TAFF) model which is found to decreases with field.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 12 | Pressure not reported | onset |
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9 | Pressure not reported | zero_resistance |
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 10 | Pressure not reported | unknown |
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Flux free growth of large FeSe1/2Te1/2 superconducting single crystals by an easy high temperature melt and slow cooling method
similarity 0.95Rajveer Jha et al. · 2015 · arXiv:1502.01813
Source status unknown — claims are unverified
Detailed physical property characterization of FeTe1-xSex x = 0.0 to 0.50 single crystals
similarity 0.92P. K. Maheshwari et al. · 2019 · arXiv:1901.04224
Source status unknown — claims are unverified
Temperature dependence of lower critical field Hc1(T) shows nodeless superconductivity in FeSe
similarity 0.92M. Abdel-Hafiez et al. · 2014 · arXiv:1409.0614
Source status unknown — claims are unverified
Structural, and Magnetic properties of flux free large FeTe Single crystal
similarity 0.91Maheshwari, P. K et al. · 2016 · arXiv:1507.03320
Source status unknown — claims are unverified
Heat capacity and Mosssbauer study of Self flux grown FeTe Single Crystal
similarity 0.91P. K Maheshwari et al. · 2018 · arXiv:1803.04615
Source status unknown — claims are unverified
Superconductivity at T_c ~ 14 K in Single Crystalline FeTeSe
similarity 0.90T. Taen et al. · 2009 · arXiv:0906.1951
Source status unknown — claims are unverified