Size Dependence of Oxygen-annealing Effects on Superconductivity of Fe{1+y}Te{1-x}S{x}
Teruo Yamazaki, Tatsuya Sakurai, Hiroshi Yaguchi
arXiv:1608.04957 · DOI 10.7566/JPSJ.85.114712 · 2016-08-17 · Journal of the Physical Society of Japan
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
For the Fe-based superconductor Fe{1+y}Te{1-x}S{x}, superconductivity is induced by annealing treatment in oxygen atmosphere, whereas as-grown samples do not show superconductivity. We have investigated the sample-size dependence of O2-annealing effects in Fe1.01Te0.91S0.09. The annealing conditions are fixed to be 1 atm, 200 C, and 2 hours. We have carried out magnetic susceptibility and specific heat measurements in order to evaluate the superconducting volume fraction. We have found that Fe{1+y}Te{1-x}S{x} has an optimal size for the induction of bulk superconductivity by O2 annealing. Our results indicate that O2 annealing is probably effective near the surface of samples over a length of a few tens of micro meters.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.8 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.4 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.4 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.4 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.2 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8 | Pressure not reported | midpoint |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.5 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.8 | Pressure not reported | midpoint |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.6 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8 | Pressure not reported | midpoint |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 10.2 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.8 | Pressure not reported | midpoint |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.2 | Pressure not reported | onset |
| Fe1.01Te0.91S0.09 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.9 | Pressure not reported | midpoint |
Similar papers
Annealing, acid, and alcoholic beverage effects on Fe1+yTe0.6Se0.4
similarity 0.91Y. Sun et al. · 2012 · arXiv:1211.3491
Source status unknown — claims are unverified
Dynamics and mechanism of oxygen annealing in FeTeSe single crystal
similarity 0.90Yue Sun et al. · 2014 · arXiv:1404.0916
Source status unknown — claims are unverified
Superconductivity in Fe1+dTe0.9Se0.1 induced by deintercalation of excess Fe using alcoholic beverage treatment
similarity 0.89K. Deguchi et al. · 2012 · arXiv:1210.5889
Source status unknown — claims are unverified
Bulk Superconductivity in FeTeSe Induced by Annealing in Se and S Vapor
similarity 0.89Yue Sun et al. · 2013 · arXiv:1310.1983
Source status unknown — claims are unverified
Clarification as to why alcoholic beverages have the ability to induce superconductivity in Fe_{1+d}Te_{1-x}S_x
similarity 0.89K. Deguchi et al. · 2012 · arXiv:1204.0190
Source status unknown — claims are unverified
Electronic properties of single-crystalline FeTe and FeSeTe
similarity 0.89G. F. Chen et al. · 2008 · arXiv:0811.1489
Source status unknown — claims are unverified