Superconducting NbTiN Thin Films with Highly Uniform Properties over a 100 mm diameter Wafer
D. J. Thoen, B. G. C. Bos, E. A. F. Haalebos, T. M. Klapwijk, J. J. A. Baselmans, A. Endo
arXiv:1609.01526 · DOI 10.1109/TASC.2016.2631948 · 2016-09-06 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Uniformity in thickness and electronic properties of superconducting niobium titanium nitride (NbTiN) thin films is a critical issue for upscaling superconducting electronics, such as microwave kinetic inductance detectors for submillimeter wave astronomy. In this article we make an experimental comparison between the uniformity of NbTiN thin films produced by two DC magnetron sputtering systems with vastly different target sizes: the Nordiko 2000 equipped with a circular 100mm diameter target, and the Evatec LLS801 with a rectangular target of 127 mm x 444.5 mm. In addition to the films deposited staticly in both systems, we have also deposited films in the LLS801 while shuttling the substrate in front of the target, with the aim of further enhancing the uniformity. Among these three setups, the LLS801 system with substrate shuttling has yielded the highest uniformity in film thickness (+/-2%), effective resistivity (decreasing by 5% from center to edge), and superconducting critical temperature (T_c = 15.0 K - 15.3 K) over a 100 mm diameter wafer. However, the shuttling appears to increase the resistivity by almost a factor of 2 compared to static deposition. Surface SEM inspections suggest that the shuttling could have induced a different mode of microstructural film growth.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| NbTiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 15.2 | Pressure not reported | unknown |
Similar papers
Reactive magnetron sputter deposition of superconducting niobium titanium nitride thin films with different target sizes
similarity 0.88B. G. C. Bos et al. · 2016 · arXiv:1609.01265
Source status unknown — claims are unverified
Structural transitions in superconducting NbTiN thin films
similarity 0.87Yeram, Siddhesh Sanjay et al. · 2023 · arXiv:2311.14154
Source status unknown — claims are unverified
Evidence of the disorder-independent electron-phonon scattering time in thin NbN films
similarity 0.86A. I. Lomakin et al. · 2022 · arXiv:2207.05012
Source status unknown — claims are unverified
Spatial homogeneity of superconducting order parameter in NbN films grown by atomic layer deposition
similarity 0.86J. Lorenz et al. · 2026 · arXiv:2602.10839
Source status unknown — claims are unverified
Dynamic fluctuations in the superconductivity of NbN films from microwave conductivity measurements
similarity 0.86Takeyoshi Ohashi et al. · 2006 · arXiv:cond-mat/0605179
Source status unknown — claims are unverified
Contactless terahertz mapping of wafer-scale superconducting NbTiN thin films
similarity 0.86Yayi Lin et al. · 2026 · arXiv:2607.15757
Source status unknown — claims are unverified