Critical Current Survival in YBCO Superconducting Layer of the Delaminated Coated Conductor
Feng Feng, Qishu Fu, Timing Qu, Chen Gu, Yubin Yue, Hui Mu, Xiangsong Zhang, Hongyuan Lu, Linli Wang, Siwei Chen, Pingfa Feng
arXiv:1612.08553 · DOI 10.1088/1361-6668/aaacc4 · 2016-12-27 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
High temperature superconducting coated conductor (CC) could be practically applied in electric equipment due to its favorable mechanical properties and the critical current performance of YBCO superconducting layer. It is well known that CC could be easily delaminated because of its poor stress tolerance in thickness direction, i.e. along the c-axis of YBCO. Commonly, a stack including YBCO layer and silver stabilizer could be obtained after the delamination. It would be interesting to investigate the superconducting properties of the delaminated stack, since it could also be considered as a new type of CC with the silver stabilizer as the buffer layer, which is quite different from the oxide buffer layers in the traditional CC and might lead to new applications. In this study, a CC sample was delaminated by liquid nitrogen immersing. A Hall probe scanning system was employed to measure the critical current (IC) distribution of the original sample and the obtained stack. It was found that IC could be partially preserved after the delamination. Dense and crack-free morphologies of the delaminated surfaces were observed by scanning electron microscopy, and the potential application of the obtained stack in superconducting joint technology was discussed.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Through-thickness superconducting and normal-state transport properties revealed by thinning of thick film ex situ YBa2Cu3O7-x coated conductors
similarity 0.87D. M. Feldmann et al. · 2003 · arXiv:cond-mat/0310123
Source status unknown — claims are unverified
The Integration of YBCO Coated Conductors into Magnets and Rotating Machinery
similarity 0.84G. A. Levin & P. N. Barnes · 2005 · arXiv:cond-mat/0509347
Source status unknown — claims are unverified
Stability and normal zone propagation speed in YBCO coated conductors with increased interfacial resistance
similarity 0.84George A. Levin et al. · 2008 · arXiv:0808.3409
Source status unknown — claims are unverified
Properties of high-Tc Josephson junctions with Y0.7Ca0.3Ba2Cu3O7−δ barrier layers
similarity 0.84L. Antognazza et al.
Source status unknown — claims are unverified
Dynamic Cooper-pair breaking by tunnel injection of quasiparticles into a high-Tc YBa2Cu3O7 superconductor
similarity 0.83I. Iguchi et al.
Source status unknown — claims are unverified
Doubling the Critical Current Density of High Temperature Superconducting Coated Conductors through Proton Irradiation
similarity 0.83Y. Jia et al. · 2013 · arXiv:1307.0847
Source status unknown — claims are unverified