Evolution of structure, magnetic and transport properties of Fe$_{1-x}$Mn$_{x}$Se

Kapil E. Ingle, K. R. Priolkar, P. A. Bhobe, A. K. Nigam

arXiv:1701.08247 · DOI 10.1088/2053-1591/3/12/126001 · 2017-01-28 · Materials Research Express

T1theoretical2 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The present paper seeks to investigate effect of Mn doping in superconducting FeSe. It is found that over the entire doping range in Fe$_{1-x}$Mn$_x$Se ($0 \le x \le 1$), Mn does not substitute Fe in the superconducting tetragonal phase. Instead two impurity phases, NiAs type hexagonal phase and NaCl type cubic phase grow with increasing Mn content. Initially, hexagonal phase has a higher content than the cubic phase but beyond $x$ = 0.5, the cubic phase grows rapidly and for $x \ge 0.8$, the sample is monophasic with cubic NaCl type structure. The superconducting tetragonal phase content steadily decreases with increasing Mn concentration and completely disappears beyond $x = 0.5$. The premise that Mn never replaces Fe in the superconducting phase is further strengthened by observation of a sharp drop in AC susceptibility akin to superconducting transition at the T$_c$ of FeSe up to $x$ = 0.5. EXAFS studies at the Fe K edge also show that the Fe has a four coordinated tetragonal local structure in all compositions below $x = 0.5$, similar to that in FeSe and it gradually changes to a six coordinated one as is expected for a NaCl type cubic phase for $x \ge 0.5$.

Source-reported materials — not catalogue approval

FormulaReported Tc (K)Pressure (GPa)Type
FeSe

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

8Pressure not reportedunknown
Fe0.98Mn0.02Se

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

8Pressure not reportedunknown
Fe0.95Mn0.05Se

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

8Pressure not reportedunknown
Fe0.9Mn0.1Se

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

8Pressure not reportedunknown
Fe0.8Mn0.2Se

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

8Pressure not reportedunknown
Fe0.7Mn0.3Se

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

8Pressure not reportedunknown
Fe0.6Mn0.4Se

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

8Pressure not reportedunknown
Fe0.5Mn0.5Se

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

8Pressure not reportedunknown

Similar papers