Various arsenic network structures in 112-type Ca1-xLaxFe1-yPdyAs2 revealed by synchrotron x-ray diffraction experiments
Shinya Tamura, Naoyuki Katayama, Yuto Yamada, Yuki Sugiyama, Kento Sugawara, Hiroshi Sawa
arXiv:1703.04204 · DOI 10.1021/acs.inorgchem.6b03115 · 2017-03-13 · Inorganic chemistry
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Two novel 112-type palladium doped iron arsenides were synthesized and identified using comprehensive studies involving synchrotron x-ray diffraction and x-ray absorption near edge structure (XANES) experiments. Whereas in-plane arsenic zigzag chains were found in 112-type superconducting iron arsenide, Ca1-xLaxFeAs2 with maximum Tc = 34 K, deformed arsenic network structures appeared in 112-type materials such as longitudinal arsenics zigzag chains in CaFe1-yPdyAs2 (y ~ 0.51) and arsenic square sheets constructed via hypervalent bonding in Ca1-xLaxFe1-yPdyAs2 (x ~ 0.31, y ~ 0.30). As K-edge XANES spectra clarified the similar oxidization states around FeAs4 tetrahedrons, expecting us the possible parents for high Tc 112-type iron arsenide superconductors.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Ca1-xLaxFeAs2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 34 | Pressure not reported | unknown |
Similar papers
Superconductivity in Ca1-xLaxFeAs2: A Novel 112-Type Iron Pnictide with Arsenic Zigzag Bonds
similarity 0.90Naoyuki Katayama et al. · 2013 · arXiv:1311.1303
Source status unknown — claims are unverified
Phase stability and large in-plane resistivity anisotropy in the 112-type iron-based superconductor Ca1−xLaxFeAs2
similarity 0.90Chang-Jong Kang et al.
Source status unknown — claims are unverified
Site-Selective Antimony Doping in Arsenic Zigzag Chains of 112-type Ca1-xLaxFeAs2
similarity 0.89Hiromi Ota et al. · 2017 · arXiv:1702.02672
Source status unknown — claims are unverified
Superconducting Transition Temperatures of up to 47 K from Simultaneous Rare-Earth Element and Antimony Doping of 112-Type CaFeAs2
similarity 0.89Kazutaka Kudo et al. · 2014 · arXiv:1408.4197
Source status unknown — claims are unverified