Growth of bulk single-crystal MnP helimagnet and its structural and NMR characterization

Nikolai D. Zhigadlo; Nicolo Barbero; Toni Shiroka

doi:10.1016/j.jallcom.2017.07.247

← Back to search

Growth of bulk single-crystal MnP helimagnet and its structural and NMR characterization

Nikolai D. Zhigadlo, Nicolo Barbero, Toni Shiroka

arXiv:1705.10491 · DOI 10.1016/j.jallcom.2017.07.247 · 2017-05-30 · Journal of Alloys and Compounds

T317 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Bulk single crystals of manganese phosphide (MnP) were grown from melt at 1 GPa and 1200 C by using a cubic-anvil, high-pressure, and high-temperature technique. The obtained black colored crystals exhibit a plate-like morphology, with flat surfaces and maximum dimensions up to 4 x 2 x 0.5 mm3. The orthorhombic crystal structure was confirmed by X-ray diffraction [Pnma, 62, Z = 4, a = 5.2510(4) Å, b = 3.1670(3) Å, c = 5.90098 (4) Å and V = 98.279(14) Å3]. Temperature-dependent magnetization measurements reveal the occurrence of two successive transitions: a paramagnetic to ferromagnetic transition at Tc = 290.5 K and the development of a double helimagnetic order at Ts = 44.5 K. Zero-field 31P NMR measurements in the FM and in the screw-spin AFM state show prominent features, which are compared with previous experimental data and theoretical calculations. The relatively large crystals obtained here open up new possibilities for further explorations of this interesting material.