Superconductivity and its Enhancement under High Pressure in "F-free" Single Crystals of CeOBiS$_2$

Masashi Tanaka; Masanori Nagao; Ryo Matsumoto; Noriyuki Kataoka; Ikuo Ueta; Hiromi Tanaka; Satoshi Watauchi; Isao Tanaka; Yoshihiko Takano

doi:10.1016/j.jallcom.2017.06.125

Superconductivity and its Enhancement under High Pressure in "F-free" Single Crystals of CeOBiS$_2$

Masashi Tanaka, Masanori Nagao, Ryo Matsumoto, Noriyuki Kataoka, Ikuo Ueta, Hiromi Tanaka, Satoshi Watauchi, Isao Tanaka, Yoshihiko Takano

arXiv:1706.03590 · DOI 10.1016/j.jallcom.2017.06.125 · 2017-06-12 · Journal of Alloys and Compounds

T1theoretical16 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

"F-free" CeOBiS$_2$ single crystals have successfully grown, thoroughly eliminating a concern about F-contamination by using a high-purity CsCl flux. The obtained crystals have a plate-like shape with a size of 1.0-3.0 mm in the well-developed plane. Single crystal X-ray structural analysis clearly revealed that the CeOBiS$_2$ crystallizes with a space group $P4/nmm$ (with lattice parameters of $a$ = 4.0189(6) Å, $c$ = 13.573(2) Å). The bond valence sum estimation and X-ray photoelectron spectroscopy analysis showed that the chemical state of Ce was in the mixed valence of Ce$^{3+}$ and Ce$^{4+}$. The single crystals show superconductivity with zero resistivity at $\sim$1.3 K. This is the first conclusive evidence of superconductivity driven by Ce valence fluctuation in surely non-doped CeOBiS$_2$. The superconducting transition temperature was enhanced up to $\sim$3.8 K by applying hydrostatic pressure.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
CeOBiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.3	Pressure not reported	zero_resistance
CeOBiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.8	Pressure not reported	unknown