X-ray photoelectron spectroscopy, Magnetotransport and Magnetization study of Nb2PdS5 superconductor

Reena Goyal, A. K. Srivastava, Monu Mishra, Govind Gupta, Rajveer Jha, V. P. S. Awana

arXiv:1711.02830 · DOI 10.1007/s10948-017-4415-8 · 2017-11-08 · Journal of Superconductivity and Novel Magnetism

T1theoretical15 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

In the present report, we investigate various properties of the Nb2PdS5 superconductor. Scanning electron microscopy displayed slabs like laminar growth of Nb2PdS5while X-ray photoelectron spectroscopy exhibited the hybridization of Sulphur (2p) with both Palladium (3d)and Niobium (3d). High field (140kOe) magneto-transport measurements revealed that superconductivity (Tc onset =7K and Tc R = 0 = 6.2K) of the studied Nb2PdS5material is quite robust against magnetic field with the upper critical field (Hc2) outside the Pauli paramagnetic limit. Thermally activated flux flow (TAFF) of the compound showed that resistivity curves follow Arrhenius behaviour. The activation energy for Nb2PdS5 is found to decrease from 15.15meV at 10kOe to 2.35meV at 140kOe. Seemingly, the single vortex pinning is dominant in low field regions, while collective pinning is dominant in high field region. The temperature dependence of AC susceptibility confirmed the Tc at 6K, further varying amplitude and frequency showed well coupled granular nature of superconductivity. The lower critical field (Hc1) is extracted from DC magnetisation measurements at various T below Tc. It is found that Hc1(T) of Nb2PdS5 material seemingly follows the multiband nature of superconductivity.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Nb2PdS5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure not reported	onset
Nb2PdS5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.2	Pressure not reported	zero_resistance
Nb2PdS5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6	Pressure not reported	unknown