Superconductivity at 3.1 K in the orthorhombic ternary silicide ScRuSi
Bin-Bin Ruan, Xiao-Chuan Wang, Jia Yu, Bo-Jin Pan, Qing-Ge Mu, Tong Liu, Gen-Fu Chen, Zhi-An Ren
arXiv:1711.05474 · DOI 10.1088/1361-6668/30/2/025008 · 2017-11-15 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report the synthesis, crystal structure, superconductivity and physical property characterizations of the ternary equiatomic compound ScRuSi. Polycrystalline samples of ScRuSi were prepared by an arc-melting method. The as-prepared samples were identified as the orthorhombic Co2P-type o-ScRuSi by the powder X-ray diffraction analysis. Electrical resistivity measurement shows o-ScRuSi to be a metal which superconducts below a Tc of 3.1 K, and the upper critical field μ0Hc2(0) is estimated to be 0.87 T. The magnetization and specific heat measurements confirm the bulk type-II superconductivity in o-ScRuSi, with the specific heat jump within the BCS weak coupling limit. o-ScRuSi is the first Co2P-type superconductor containing scandium. After annealing at 1273 K for a week, o-ScRuSi transforms into the hexagonal Fe2P-type h-ScRuSi, and the latter is a Pauli-paramagnetic metal with no superconductivity observed above 1.8 K.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| ScRuSi Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 3.1 | Pressure not reported | unknown |
Similar papers
dc electrical resistivity and upper critical magnetic field of superconducting ternary silicides and germanides with the Sc5Co4Si10-type structure
similarity 0.89L. S. Hausermann-Berg & R. N. Shelton
Source status unknown — claims are unverified
First-principles calculations of physical properties and superconductivity of orthorhombic ScRuSi and ZrRhSi
similarity 0.88H. Y. Uzunok et al.
Source status unknown — claims are unverified
Probing the superconducting gap structure of ScRuSi via μSR and first-principles calculations
similarity 0.88K. Panda et al.
Source status unknown — claims are unverified
Synthesis and superconductivity of new BiS2 based superconductor PrO0.5F0.5BiS2
similarity 0.86Rajveer Jha et al. · 2012 · arXiv:1208.5873
Source status unknown — claims are unverified
Record High 36 K Transition Temperature to the Superconducting State of Elemental Scandium at a Pressure of 260 GPa
similarity 0.85Jianjun Ying et al.
Source status unknown — claims are unverified
Superconductivity in bismuth-strontium-copper oxides
similarity 0.85J. P. Franck et al.
Source status unknown — claims are unverified