Transport properties of ultrathin BaFe1.84Co0.16As2 superconducting nanowires
Pusheng Yuan, Zhongtang Xu, Chen Li, Baogang Quan, Junjie Li, Changzhi Gu, Yanwei Ma
arXiv:1711.07637 · DOI 10.1088/1361-6668/aa9b61 · 2017-11-21 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconducting nanowire single-photon detectors (SNSPDs) have an absolute advantage over other types of single photon detectors except the low operating temperature. Therefore, many efforts have been devoted to find high-temperature superconducting materials that are suitable for preparing SNSPDs. Copper-based and MgB2 ultra-thin superconducting nanowires have been already reported. However, the transport properties of iron-based ultra-thin superconducting nanowires have not been studied. In this work, a 10 nm thick 200 nm wide 30 μm long high quality superconducting nanowire was fabricated from ultrathin BaFe1.84Co0.16As2 films by a lift-off process. The precursor BaFe1.84Co0.16As2 film with a thickness of 10 nm and root-mean-square roughness of 1 nm was grown on CaF2 substrates by pulsed laser deposition. The nanowire shows a high superconducting critical temperature Tzero c=20 K with a narrow transition width of Delta T=2.5 K and exhibits a high critical current density Jc of 1.8E7 A/cm2 at 10 K. These results of ultrathin BaFe1.84Co0.16As2 nanowire will attract interest in electronic applications, including SNSPDs
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| BaFe1.84Co0.16As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 20 | Pressure not reported | zero_resistance |
Similar papers
Inhomogeneous critical current in nanowire superconducting single-photon detectors
similarity 0.88Rosalinda Gaudio et al. · 2014 · arXiv:1412.0416
Source status unknown — claims are unverified
NbN superconducting nanowire single photon detector with efficiency over 90% at 1550 nm wavelength operational at compact cryocooler temperature
similarity 0.87W. J. Zhang et al. · 2016 · arXiv:1609.00429
Source status unknown — claims are unverified
Low kinetic inductance superconducting nanowire photon detectors with a 100 picosecond relaxation time
similarity 0.87Sergey Cherednichenko et al. · 2019 · arXiv:1911.01480
Source status unknown — claims are unverified
Transport properties of ultrathin YBaCuO nanowires: a route to single photon detection
similarity 0.87Riccardo Arpaia et al. · 2017 · arXiv:1708.04721
Source status unknown — claims are unverified
Superconducting nanowire single-photon detectors at a wavelength of 940 nm
similarity 0.86W. J. Zhang et al. · 2015 · arXiv:1506.07921
Source status unknown — claims are unverified
Characterization of the thin-film NbN superconductor for single-photon detection by transport measurements
similarity 0.86Shi-Zeng Lin et al.
Source status unknown — claims are unverified