Superconductivity in Cage Compounds La$Tr_{2}$Al$_{20}$ with $Tr$ = Ti, V, Nb, and Ta

Akira Yamada; Ryuji Higashinaka; Tatsuma D. Matsuda; Yuji Aoki

doi:10.7566/JPSJ.87.033707

← Back to search

Superconductivity in Cage Compounds La$Tr_{2}$Al$_{20}$ with $Tr$ = Ti, V, Nb, and Ta

Akira Yamada, Ryuji Higashinaka, Tatsuma D. Matsuda, Yuji Aoki

arXiv:1802.06119 · DOI 10.7566/JPSJ.87.033707 · 2018-02-16 · Journal of the Physical Society of Japan

T2experimental16 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Electrical resistivity, magnetic susceptibility, and specific heat measurements on single crystals of La$Tr_{2}$Al$_{20}$ ($Tr$ = Ti, V, Nb, and Ta) revealed that these four compounds exhibit weak-coupling superconductivity with transition temperatures $T_{\rm c}$ = 0.46, 0.15, 1.05, and 1.03 K, respectively. LaTi$_{2}$Al$_{20}$ is most probably a type-I superconductor, which is quite rare among intermetallic compounds. Single-crystal X-ray diffraction suggests "rattling" anharmonic large-amplitude oscillations of Al ions (16$c$ site) on the Al$_{16}$ cage, while no such feature is suggested for the cage-center La ion. Using a parameter $d_{\rm GFS}$ quantifying the "guest free space" of the cage-center ion, we demonstrate that nonmagnetic $RTr_{2}$Al$_{20}$ superconductors are classified into two groups, i.e., (A) $d_{\rm GFS} \ne 0$ and $T_{\rm c}$ correlates with $d_{\rm GFS}$, and (B) $d_{\rm GFS} \simeq 0$ and $T_{\rm c}$ seems to be governed by other factors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaTi2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.46	Pressure not reported	onset
LaTi2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.3	Pressure not reported	midpoint
LaTi2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.46	Pressure not reported	unknown
LaV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.15	Pressure not reported	onset
LaV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.15	Pressure not reported	midpoint
LaV2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.15	Pressure not reported	unknown
LaNb2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.05	Pressure not reported	onset
LaNb2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.15	Pressure not reported	midpoint
LaNb2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.05	Pressure not reported	unknown
LaTa2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.03	Pressure not reported	onset
LaTa2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.1	Pressure not reported	midpoint
LaTa2Al20 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.03	Pressure not reported	unknown