Thermodynamics analysis on BaF2 intermediate phase in solution-derived YBCO superconducting film deposition
Feng Feng, Hongyuan Lu, Wei Wu, Xiangsong Zhang, Linli Wang
arXiv:1802.07467 · 2018-02-21 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
In the YBa2Cu3O7-δ (YBCO) high temperature superconducting thin film fabrication via the chemical solution deposition method, BaF2 is an important intermediate phase during heat treatment. In this paper, BaF2 thermodynamics stability was analyzed through calculating the standard Gibbs free energy change (ΔGT) of the reactions related to other intermediate phases within the temperature range of 700-1000 K. Two thermodynamics methods, the Gibbs free energy function method and standard formation molar Gibbs free energy method, were utilized to obtain the ΔGT values. The formation priority of BaF2 relative to other intermediate phases were verified at higher temperatures, while the possibility of BaCO3 formation was found at 700 K.
Similar papers
YBCO-buffered NdBCO film with higher thermal stability in seeding REBCO Growth
similarity 0.84H. H. Xu et al. · 2011 · arXiv:1110.6580
Source status unknown — claims are unverified
Structure of ultrathin heteroepitaxial superconducting YBa2Cu3O7−x films
similarity 0.84C. M. Schlepütz et al.
Source status unknown — claims are unverified
Thermodynamic signature of a phase transition in the pseudogap phase of high- superconductor
similarity 0.84B. Leridon et al. · 2008 · arXiv:0806.2128
Source status unknown — claims are unverified
Realization of epitaxial thin films of the superconductor K-doped BaFe2As2
similarity 0.83Dongyi Qin et al.
Source status unknown — claims are unverified
Superconductivity above 90 K in the compound YBa2Cu3Ox: Structural, transport, and magnetic properties
similarity 0.83P. M. Grant et al.
Source status unknown — claims are unverified
Magnetism and microstructure of YBa2Cu3O7−x superconductors produced by rapid solidification
similarity 0.83M. E. McHenry et al.
Source status unknown — claims are unverified