Superconductivity at 215 K in lanthanum hydride at high pressures

A. P. Drozdov; V. S. Minkov; S. P. Besedin; P. P. Kong; M. A. Kuzovnikov; D. A. Knyazev; M. I. Eremets

Superconductivity at 215 K in lanthanum hydride at high pressures

A. P. Drozdov, V. S. Minkov, S. P. Besedin, P. P. Kong, M. A. Kuzovnikov, D. A. Knyazev, M. I. Eremets

arXiv:1808.07039 · 2018-08-21

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We synthesized lanthanum hydride (LaHx) by laser heating of lanthanum in hydrogen atmosphere at pressure P = 170 GPa. The sample shows a superconducting step at 209 K and 170 GPa and temperature dependence of resistance. By releasing the pressure to 150 GPa, the superconducting transition temperature Tc increases to 215 K - the record Tc. This finding supports a way of achieving Tc higher than the one in H3S (203 K) in hydrides with sodalite-like structures, first proposed for CaH6 (Tc=245 K) and later for yttrium and lanthanum hydrides where higher, room temperature superconductivity is expected.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaHx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	209	170 GPa	onset
LaHx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	215	150 GPa	onset
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	203	Pressure not reported	unknown
CaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	245	Pressure not reported	unknown