Supercondutivity in SnSb with natural superlattice structure

Bin Liu; Jifeng Wu; Yanwei Cui; Hangdong Wang; Yi Liu; Zhicheng Wang; Zhi Ren; Guanghan Cao

Supercondutivity in SnSb with natural superlattice structure

Bin Liu, Jifeng Wu, Yanwei Cui, Hangdong Wang, Yi Liu, Zhicheng Wang, Zhi Ren, Guanghan Cao

arXiv:1808.08500 · 2018-08-26

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report the results of electrical resistivity, magnetic and thermodynamic measurements on polycrystalline SnSb, whose structure consists of stacks of Sb bilayers and Sn4Sb3 septuple layers along the c-axis. The material is found to be a weakly coupled, fully gapped, type-II superconductor with a bulk Tc of 1.50 K, while showing a zero resistivity transition at a significantly higher temperature of 2.48 K. The Sommerfeld coefficient and upper critical field, obtained from specific heat measurements, are 2.29 mJ/mol K and 520 Oe, respectively. Compositional inhomogeneity and strain effect at the grain boundaries are proposed as possible origins for the difference in resistive and bulk superconducting transitions.In addition, a comparison with the rock-salt structure SnAs superconductor is presented. Our results provide the first clear evidence of bulk superconductivity in a natural superlattice derived from a topological semimetal.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
SnSb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.48	Pressure unresolved	midpoint
SnSb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.5	Pressure unresolved	unknown
SnSb Archive — disputed claim Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
SnAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown