Superconductivity in doped FeTe1-xSx (x= 0.00 to 0.25) single crystals

P. K Maheshwar; V. Raghavendra Reddy; B. Gahtori; V. P. S. Awana

doi:10.1088/2053-1591/aae244

← Back to search

Superconductivity in doped FeTe1-xSx (x= 0.00 to 0.25) single crystals

P. K Maheshwar, V. Raghavendra Reddy, B. Gahtori, V. P. S. Awana

arXiv:1809.06116 · DOI 10.1088/2053-1591/aae244 · 2018-09-17 · Materials Research Express

T1experimental7 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report self flux growth and characterization of FeTe1-xSx (x= 0.00 to 0.25) single crystal series. Surface X-ray diffraction (XRD) exhibited crystalline nature with growth in (00l) plane. Micro-structural (electron microscopy) images of representative crystals showed the slab-like morphology and near stoichiometric composition. Powder XRD analysis (Rietveld) of single crystals exhibited tetragonal structure with P4/nmm space group and decreasing a and c lattice parameters with increase in x. Electrical resistivity measurements (R-T) showed superconductivity with Tconset at 9.5K and 8.5K for x =0.10 and x =0.25 respectively. The un-doped crystal exhibited known step like anomaly at around 70K. Upper critical field Hc2(0), as calculated from magneto transport for x =0.25 crystal is around 60Tesla and 45Tesla in H//ab and H//c directions. Thermal activation energy [U0(H)] calculated for x =0.10 and 0.25 crystals followed weak power law, indicating single vortex pinning at low fields. Mossbauer spectra for FeTe1-xSx crystals at 300K and 5K are compared with non superconducting FeTe. Both quadrupole splitting (QS) and isomer shift (IS) for S doped crystals were found to decrease. Also at 5K the hyperfine field for x =0.10 superconducting crystal is decreased substantially from 10.6Tesla (FeTe) to 7.2Tesla. For x =0.25 crystal, though small quantity of un-reacted Fe is visible at room temperature, but unlike x =0.10, the low temperature (5K) ordered FeTe hyperfine field is nearly zero.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeTe0.9S0.1 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.5	Pressure not reported	onset
FeTe0.75S0.25 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure not reported	onset