High-Temperature Superconductivity in Alkaline and Rare Earth Polyhydrides at High Pressure: A Theoretical Perspective

Eva Zurek; Tiange Bi

doi:10.1063/1.5079225

← Back to search

High-Temperature Superconductivity in Alkaline and Rare Earth Polyhydrides at High Pressure: A Theoretical Perspective

Eva Zurek, Tiange Bi

arXiv:1810.12338 · DOI 10.1063/1.5079225 · 2018-10-29 · The Journal of chemical physics

T4review154 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The theoretical exploration of the phase diagrams of binary hydrides under pressure using \emph{ab initio} crystal structure prediction techniques coupled with first-principles calculations has led to the \emph{in silico} discovery of numerous novel superconducting materials. This Perspective article focuses on the alkaline earth and rare earth polyhydrides whose superconducting critical temperature, $T_c$, was predicted to be above the boiling point of liquid nitrogen. After providing a brief overview of the computational protocol used to predict the structures of stable and metastable hydrides under pressure, we outline the equations that can be employed to estimate $T_c$. The systems with a high $T_c$ can be classified according to the motifs found in their hydrogenic lattices. The highest $T_c$s are found for cages that are reminiscent of clathrates, and the lowest for systems that contain atomic and molecular hydrogen. A wide variety of hydrogenic motifs including 1- and 2-dimensional lattices, as well as H$_{10}^{δ-}$ molecular units comprised of fused H$_5^{δ-}$ pentagons are present in phases with intermediate $T_c$s. Some of these phases are predicted to be superconducting at room temperature. Some may have recently been synthesized in diamond anvil cells.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
MgH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	263	300 GPa	unknown
CaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	227.5	150 GPa	unknown
SrH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	156	250 GPa	unknown
ScH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	135	350 GPa	unknown
ScH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	169	350 GPa	unknown
ScH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	138.5	285 GPa	unknown
ScH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	95	300 GPa	unknown
YH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	257.5	120 GPa	unknown
ZrH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	114	295 GPa	unknown
LaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	155	100 GPa	unknown
ScH9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	170	400 GPa	unknown
YH9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	264.5	150 GPa	unknown
YH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	295	400 GPa	unknown
YH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	254.5	250 GPa	unknown
YH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	315.5	250 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	288	200 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	228.5	210 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	280	210 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	209	200 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	237	200 GPa	unknown
AcH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	190.55	200 GPa	unknown
AcH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	238.5	200 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	262.5	195 GPa	unknown
LaHx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	215	150 GPa	unknown