Influence of carbon-ion irradiation on the superconducting critical properties of MgB$_2$ thin films
Soon-Gil Jung, Seung-Ku Son, Duong Pham, Weon Cheol Lim, Jonghan Song, Won Nam Kang, Tuson Park
arXiv:1811.05814 · DOI 10.1088/1361-6668/aaf2c4 · 2018-11-14 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We investigate the influence of carbon-ion irradiation on the superconducting critical properties of MgB$_2$ thin films. MgB$_2$ films of two thicknesses viz. 400 nm (MB400nm) and 800 nm (MB800nm) were irradiated by 350 keV C ions having a wide range of fluence, 1 x 10$^{13}$ - 1 x 10$^{15}$ C atoms/cm$^2$. The mean projected range ($R_p$) of 350 keV C ions in MgB$_2$ is 560 nm, thus the energetic C ions will pass through the MB400nm, whereas the ions will remain into the MB800nm. The superconducting transition temperature ($T_c$), upper critical field ($H_{c2}$), $c$-axis lattice parameter, and corrected residual resistivity ($ρ_{corr}$) of both the films showed similar trends with the variation of fluence. However, a disparate behavior in the superconducting phase transition was observed in the MB800nm when the fluence was larger than 1 x 10$^{14}$ C atoms/cm$^2$ because of the different Tcs between the irradiated and non-irradiated parts of the film. Interestingly, the superconducting critical properties, such as $T_c$, $H_{c2}$, and $J_c$, of the irradiated MgB$_2$ films, as well as the lattice parameter, were almost restored to those in the pristine state after a thermal annealing procedure. These results demonstrate that the atomic lattice distortion induced by C-ion irradiation is the main reason for the change in the superconducting properties of MgB$_2$ films.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Roles of Fe-ion irradiation on MgB thin films: Structural, superconducting, and optical properties
similarity 0.94Dzung T. Tran et al. · 2025 · arXiv:2509.19697
Source status unknown — claims are unverified
Superconducting and Normal State Properties of Neutron Irradiated MgB2
similarity 0.89R. H. T. Wilke et al. · 2005 · arXiv:cond-mat/0507185
Source status unknown — claims are unverified
Growth of superconducting MgB2 thin films via postannealing techniques
similarity 0.89W. N. Kang et al. · 2002 · arXiv:cond-mat/0209226
Source status unknown — claims are unverified
Neutron Irradiation of MgB2 Bulk Superconductors
similarity 0.89M. Eisterer et al. · 2001 · arXiv:cond-mat/0112121
Source status unknown — claims are unverified
Superconducting properties of MgB probed by radiation-induced disordering
similarity 0.89A. E. Karkin et al. · 2001 · arXiv:cond-mat/0103344
Source status unknown — claims are unverified
Neutron Irradiation of Mg11B2 : From the Enhancement to the Suppression of Superconducting Properties
similarity 0.88M. Putti et al. · 2004 · arXiv:cond-mat/0411383
Source status unknown — claims are unverified