Growth and Characterization of Fe0.95Se0.6Te0.4 Single Crystal

Anmol Shukla; Vishal K. Maurya; Rajendra S. Dhaka

doi:10.1063/1.5113249

← Back to search

Growth and Characterization of Fe0.95Se0.6Te0.4 Single Crystal

Anmol Shukla, Vishal K. Maurya, Rajendra S. Dhaka

arXiv:1901.01955 · DOI 10.1063/1.5113249 · 2019-01-07 · DAE SOLID STATE PHYSICS SYMPOSIUM 2018

T1experimental1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

In this paper we present the single crystal growth of Fe0.95Se0.6Te0.4 high TC superconducting sample by the modified Bridgman technique. The x-ray diffraction pattern shows the single crystal nature of the sample, as only (00l) peaks are detectable. The stoichiometric composition has been verified by energy dispersive x-ray analysis. The superconducting transition temperature at 14 K was confirmed through DC magnetization (ZFC-FC) and resistivity measurements. By analyzing the isothermal M-H curves, we determined the value of H_c1 (0) ~360 Oe by extrapolating the data. The temperature coefficient of resistivity obtained using the power law fitting was found to be 0.6. The obtained Raman spectra at room temperature can be interpreted with the tetragonal crystal structure and space group P4/nmm.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Fe0.95Se0.6Te0.4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14	Pressure not reported	unknown
Fe0.95Se0.6Te0.4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14	Pressure not reported	unknown