Superconductivity of Electron-Doped NdOBiS2 by Substitution of Mixed-Valence Ce ions

Naoki Kase; Masaya Matsumoto; Katsuo Kondo; Jun Gouchi; Yoshiya Uwatoko; Toshiro Sakakibara; Nobuaki Miyakawa

doi:10.7566/JPSJ.88.103703

← Back to search

Superconductivity of Electron-Doped NdOBiS2 by Substitution of Mixed-Valence Ce ions

Naoki Kase, Masaya Matsumoto, Katsuo Kondo, Jun Gouchi, Yoshiya Uwatoko, Toshiro Sakakibara, Nobuaki Miyakawa

arXiv:1909.01710 · DOI 10.7566/JPSJ.88.103703 · 2019-09-04 · Journal of the Physical Society of Japan

T1experimental3 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Superconductivity is achieved in Nd1-xCexOBiS2 via electron doping using mixed-valence Ce ions. Single crystals with x = 0.2, 0.3, 0.4, and 0.5 are generated using a CsCl flux method. Plate-like single crystals with dimensions of 0.8 0.8 0.2 mm3 were obtained. The magnetic susceptibility chi(T) indicates large diamagnetism, and the electrical resistivity rho(T) indicates zero resistivity. The maximum value of Tc is observed at 4.7 K in Nd0.8Ce0.2OBiS2 from chi(T). From the rho(T) measurements taken in several magnetic fields, the upper critical field mu0Hc2(0) is estimated to be about 12 and 0.34 T for the ab- and c-planes, respectively. We redetermined mu0Hc2(0) of NdO0.7F0.3BiS2, as about 35 and 0.78 T for the ab- and c-planes, respectively. The anisotropic parameter is estimated to be about 35 for Nd0.7Ce0.3OBiS2 and 45 for NdO0.7F0.3BiS2. The mu0Hc2(0) of Nd0.7Ce0.3OBiS2 is approximately two times smaller than that of NdO0.7F0.3BiS2, although the difference of Gamma is approximately 10.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Nd0.8Ce0.2OBiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.7	Pressure not reported	onset
Nd0.7Ce0.3OBiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
NdO0.7F0.3BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown