High-Temperature Superconductivity in the Ti--H System at High Pressures

Jin Zhang; Jeffrey M. McMahon; Artem R. Oganov; Xinfeng Li; Xiao Dong; Huafeng Dong; Shengnan Wang

doi:10.1103/PHYSREVB.101.134108

← Back to search

High-Temperature Superconductivity in the Ti--H System at High Pressures

Jin Zhang, Jeffrey M. McMahon, Artem R. Oganov, Xinfeng Li, Xiao Dong, Huafeng Dong, Shengnan Wang

arXiv:1911.09293 · DOI 10.1103/PHYSREVB.101.134108 · 2019-11-21 · Physical Review B

T3theoretical22 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Search for stable high-pressure compounds in the Ti--H system reveals the existence of titanium hydrides with new stoichiometries, including Ibam-Ti$_2$H$_5$, I4/m-Ti$_5$H$_{13}$, I$\bar{4}$-Ti$_5$H$_{14}$, Fddd-TiH$_4$, Immm-Ti$_2$H$_{13}$, P$\bar{1}$-TiH$_{12}$, and C2/m-TiH$_{22}$. Our calculations predict I4/mmm $\rightarrow$ R$\bar{3}$m and I4/mmm $\rightarrow$ Cmma transitions in TiH and TiH$_2$, respectively. Phonons and the electron--phonon coupling of all searched titanium hydrides are analyzed at high pressure. It is found that Immm-Ti$_2$H$_{13}$ rather than the highest hydrogen content C2/m-TiH$_{22}$, exhibits the highest superconducting critical temperature T$_{c}$. The estimated T$_{c}$ of Immm-Ti$_2$H$_{13}$ and C2/m-TiH$_{22}$ are respectively 127.4--149.4 K ($μ^{*}$=0.1-0.15) at 350 GPa and 91.3--110.2 K at 250 GPa by numerically solving the Eliashberg equations. One of the effects of pressure on T$_{c}$ can be attributed to the softening and hardening of phonons with increasing pressure.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Ti2H13 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	138.4	350 GPa	unknown
TiH22 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	100.75	250 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	197.5	200 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	203	150 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	280	210 GPa	unknown
YH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	315.5	250 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	255	185 GPa	unknown
LiH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	82	300 GPa	unknown
MgH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	271	400 GPa	unknown
CaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	227.5	150 GPa	unknown
ScH9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	233	300 GPa	unknown
ZrH Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	11	120 GPa	unknown
HfH2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12	260 GPa	unknown
TaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	130	300 GPa	unknown
GeH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	140	180 GPa	unknown
LaH16 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	156	200 GPa	unknown
SnH14 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	91.5	300 GPa	unknown
H3Se Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	131	200 GPa	unknown
H4Te Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	99.5	170 GPa	unknown
TiH2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.7	Pressure unresolved	unknown
TiH2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.002	Pressure unresolved	unknown