Yuta Shukunami; Aichi Yamashita; Yosuke Goto; Yoshikazu Mizuguchi

doi:10.1016/j.physc.2020.1353623

← Back to search

Synthesis of RE123 high-Tc superconductors with a high-entropy-alloy-type RE site

Yuta Shukunami, Aichi Yamashita, Yosuke Goto, Yoshikazu Mizuguchi

arXiv:2001.08365 · DOI 10.1016/j.physc.2020.1353623 · 2020-01-23 · Physica C: Superconductivity and its Applications

T1theoretical45 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We have synthesized high-entropy-alloy-type (HEA-type) RE123 superconductors Y0.28Nd0.16Sm0.18Eu0.18Gd0.20Ba2Cu3O7-d and Y0.18La0.24Nd0.14Sm0.14Eu0.15Gd0.15Ba2Cu3O7-d with a superconducting transition temperature (Tc) exceeding 90 K. From comparison between HEA-type and conventional RE123 samples, we found that the mixing entropy at the rare earth site does not affect Tc and critical current density (Jc) of the RE123 samples. For all the examined samples, orthorhombicity was found to be an essential parameter for Tc and Jc. In the regime near orthorhombic-tetragonal boundary, Jc for the HEA-type sample was larger than that of conventional-type samples, which suggests that HEA-type RE123 may be useful to improve Jc in the structure with low orthorhombicity.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Y0.28Nd0.16Sm0.18Eu0.18Gd0.20Ba2Cu3O7-d Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Y0.18La0.24Nd0.14Sm0.14Eu0.15Gd0.15Ba2Cu3O7-d Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown