Predicting novel superconducting hydrides using machine learning approaches

Michael J. Hutcheon; Alice M. Shipley; Richard J. Needs

doi:10.1103/PhysRevB.101.144505

← Back to search

Predicting novel superconducting hydrides using machine learning approaches

Michael J. Hutcheon, Alice M. Shipley, Richard J. Needs

arXiv:2001.09852 · DOI 10.1103/PhysRevB.101.144505 · 2020-01-27 · Physical Review B

T1computational50 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Searching for superconducting hydrides has so far largely focused on finding materials exhibiting the highest possible critical temperatures ($T_c$). This has led to a bias towards materials stabilised at very high pressures, which introduces a number of technical difficulties in experiment. Here we apply machine learning methods in an effort to identify superconducting hydrides which can operate closer to ambient conditions. The output of these models informs structure searches, from which we identify and screen stable candidates before performing electron-phonon calculations to obtain $T_c$. Hydrides of alkali and alkaline earth metals are identified as particularly promising; a $T_c$ of up to 115 K is calculated for RbH$_{12}$ at 50 GPa and a $T_c$ of up to 90 K is calculated for CsH$_7$ at 100 GPa.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
RbH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	108	50 GPa	unknown
RbH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	129	100 GPa	unknown
RbH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	133	150 GPa	unknown
RbH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	82	100 GPa	unknown
RbH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	115	50 GPa	unknown
RbH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	119	100 GPa	unknown
RbH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	126	150 GPa	unknown
CsH7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	90	100 GPa	unknown
CsH7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	34	100 GPa	unknown
CsH7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	33	100 GPa	unknown
CsH7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10	100 GPa	unknown
CsH7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5	100 GPa	unknown
CsH7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	89	100 GPa	unknown
RbH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	100 GPa	unknown
RbH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	100 GPa	unknown