Anisotropy of the transport properties of NdFeAs(O,F) thin films grown on vicinal substrates

Kazumasa Iida; Takuya Matsumoto; Keisuke Kondo; Takafumi Hatano; Hiroshi Ikuta

doi:10.1088/1361-6668/ab785c

← Back to search

Anisotropy of the transport properties of NdFeAs(O,F) thin films grown on vicinal substrates

Kazumasa Iida, Takuya Matsumoto, Keisuke Kondo, Takafumi Hatano, Hiroshi Ikuta

arXiv:2003.09105 · DOI 10.1088/1361-6668/ab785c · 2020-03-20 · Superconductor Science and Technology

T1experimental2 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

NdFeAs(O,F) thin films having different fluorine contents were grown on 5 deg. or 10 deg. vicinal cut MgO and CaF2 single crystalline substrates by molecular beam epitaxy. Structural characterisations by reflection high-energy electron diffraction and x-ray diffraction confirmed the epitaxial growth of NdFeAs(O,F). The resistivities of the ab-plane and along the c-axis were derived from the resistivity measurements in the longitudinal and transversal directions. The c-axis resistivity was always higher than the ab-plane resistivity, resulting from the anisotropic electronic structure. The resistivity anisotropy at 300 K was almost constant in the range of 50-90 irrespective of the F content. On the other hand, the resistivity anisotropy at 56 K showed a strong fluorine dependence: the resistivity anisotropy was over 200 for the films with optimum F contents (superconducting transition temperature Tc around 50 K), whereas the resistivity anisotropy was around 70 for the films in the under-doped regime (Tc between 35 and 45 K). The mass anisotropy are the effective masses along the c-axis and on the ab-plane) close to Tc derived from the anisotropic Ginzburg-Landau approach using the angular-dependency of the ab-plane resistivity was in the range from 2 to 5. On the assumption that the square of the mass anisotropy is equal to the resistivity anisotropy, those values are small compared to the normal state anisotropy.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
NdFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36	Pressure not reported	onset
NdFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	42	Pressure not reported	onset
NdFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	43	Pressure not reported	onset
NdFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	44	Pressure not reported	onset
NdFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	45	Pressure not reported	onset
NdFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	46	Pressure not reported	onset
NdFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	49	Pressure not reported	onset
NdFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	56	Pressure not reported	onset
SmFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	58	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
FeSe1-xTex Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14.2	Pressure not reported	unknown
LiFeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	19.7	Pressure not reported	unknown
BaFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
PrFeAsO0.7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
SmFeAsO0.9H0.1 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Bi2Sr2CaCu2O8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
YBa2Cu3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Fe(Se,Te) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown