A Metastable CaSH$_3$ Phase Composed of HS Honeycomb Sheets that is Superconducting Under Pressure

Yan Yan; Tiange Bi; Nisha Geng; Xiaoyu Wang; Eva Zurek

doi:10.1021/acs.jpclett.0c02299

← Back to search

A Metastable CaSH$_3$ Phase Composed of HS Honeycomb Sheets that is Superconducting Under Pressure

Yan Yan, Tiange Bi, Nisha Geng, Xiaoyu Wang, Eva Zurek

arXiv:2012.14985 · DOI 10.1021/acs.jpclett.0c02299 · 2020-12-30 · The journal of physical chemistry letters

T1experimental27 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Evolutionary searches predicted a number of ternary phases that could be synthesized at pressures of 100-300~GPa. $P6_3/mmc$ CaSH$_2$, $Pnma$ CaSH$_2$, $Cmc2_1$ CaSH$_6$, and $I\bar{4}$ CaSH$_{20}$ were composed of a Ca-S lattice along with H$_2$ molecules coordinated in a ``side-on'' fashion to Ca. The H-H bond lengths in these semiconducting phases were elongated because of H$_2$ $σ\rightarrow$ Ca d donation, and Ca d$\rightarrow$ H$_2$ $σ^*$ back-donation, via a Kubas-like mechanism. $P\bar{6}m2$ CaSH$_3$, consisting of two-dimensional HS and CaH$_2$ sheets, was metastable and metallic above \edit{128~GPa}. The presence of van Hove singularities increased its density of states at the Fermi level, and concomitantly the superconducting critical temperature, which was estimated to be as high as \edit{$\sim$100~K at 128~GPa}. This work will inspire the search for superconductivity in materials based upon \edit{honeycomb HX (X=S, Se, Te), and MH$_2$ (M=Mg, Ca, Sr, Ba) layers} under pressure.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
CaSH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	97.5	128 GPa	unknown
CaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	227.5	150 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	203	150 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	255	200 GPa	unknown
LiPH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	167	200 GPa	unknown
LiP2H14 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	169	230 GPa	unknown
Li2MgH16 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	473	250 GPa	unknown
MgCH4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	121	105 GPa	unknown
H3P0.15S0.85 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	197	200 GPa	unknown
CaYH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	258	200 GPa	unknown