Crystal Growth and High-Pressure Effects of Bi-Based Superconducting Whiskers
Ryo Matsumoto, Sayaka Yamamoto, Yoshihiko Takano, Hiromi Tanaka
arXiv:2104.01602 · DOI 10.1021/acsomega.1c00880 · 2021-04-04 · ACS Omega
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Three growth methods were tested for producing high-transition temperature superconducting Bi$_2$Sr$_2$Ca$_{n-1}$Cu$_n$O$_{2n+4+δ}$ whiskers, employing different ways to focus a compressive stress and size effect of the precursors. First, thermographic imaging was used to investigate thermal stress from temperature distribution in the precursors during growth annealing. To enhance thermal stress in the precursors, a thermal cycling method and an Ag-paste coating method were proposed and found to significantly accelerate the whisker growth. The use of pulverized precursors also promoted whisker growth, possibly due to contribution from the vapor-liquid-solid growth mechanism. The obtained whiskers revealed the typical composition, diffraction patterns, and superconducting properties of the Bi-2212 phase. The proposed methods were able to stably produce longer whiskers compared to the conventional method. Using the obtained whiskers, electrical transport measurements under high pressure were successfully performed at up to around 50 GPa.
Similar papers
Crystal Growth of BiSrCaCuO Whiskers from Pulverized Amorphous Precursors
similarity 0.95Ryo Matsumoto et al. · 2019 · arXiv:1909.00304
Source status unknown — claims are unverified
Crystal Size Improvement of Bi-based Superconducting Whiskers under Stress-controlled Condition
similarity 0.95Sayaka Yamamoto et al. · 2019 · arXiv:1911.00224
Source status unknown — claims are unverified
Growth and characterization of BiSCCO 2212 whiskers from melts containing various La contents
similarity 0.88H. Jin et al. · 1999 · arXiv:cond-mat/9909076
Source status unknown — claims are unverified
Peak effect of critical current densities of Bi2Sr2CaCu2O8+δ superconducting whiskers at high temperatures in a low-field regime
similarity 0.88M. Tange et al.
Source status unknown — claims are unverified
Evidence of Structural Instability Near T*~250 K in the Resistivity of Bi_2Sr_2CaCu_2O_8 Whiskers
similarity 0.87Weimin Chen et al. · 1999 · arXiv:cond-mat/9906079
Source status unknown — claims are unverified
Field penetration and surface barriers in superconducting Bi2Sr2CaCu2O8+δ whiskers
similarity 0.87M. S. James et al.
Source status unknown — claims are unverified