Trapping a magnetic field of 14.8 T using stacked coated conductors of 12 mm width
Masahiro Suyama, Sunseng Pyon, Yasuhiro Iijima, Satoshi Awaji, Tsuyoshi Tamegai
arXiv:2104.13042 · DOI 10.1088/1361-6668/abf621 · 2021-04-27 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We fabricated a compact (13$\times$12$\times$12.5 mm${^3}$) trapped-field magnet by stacking 200 pieces of EuBa${_2}$Cu${_3}$O${_7}$ coated conductors with BaHfO${_3}$ nanorods as artificial pinning centers. It was magnetized by field-cooling method using a 18 T superconducting magnet, and the maximum field of 14.8 T was trapped at 10 K at a field-ramp rate of 0.1 T/min. At higher temperatures, although the trapped field was decreased, we could trap the field with much faster ramp rate. In order to understand these results, we also performed calculations of the trapped field based on $J_\mathrm{c}-H$ characteristics of the coated conductor. The calculated trapped field value was larger than the experimental value at 10 K. This discrepancy can be understood by considering the reduction of the effective size of the stacked coated conductors due to the existence of extended regions of irregular flux penetration called "flux jets".
Similar papers
Superconducting trapped-field magnets: Temperature and field distributions during pulsed field activation
similarity 0.87S. Braeck et al. · 2002 · arXiv:cond-mat/0205229
Source status unknown — claims are unverified
A Trapped Field of 17.6 T in Melt-Processed, Bulk Gd-Ba-Cu-O Reinforced with Shrink-Fit Steel
similarity 0.86John H. Durrell et al. · 2014 · arXiv:1406.0686
Source status unknown — claims are unverified
Flux trapping in superconducting hydrides under high pressure
similarity 0.84J. E. Hirsch & F. Marsiglio · 2021 · arXiv:2104.03925
Source status unknown — claims are unverified
35.4 T field generated using a layer-wound superconducting coil made of (RE)Ba2Cu3O7-x (RE = Rare Earth) coated conductor
similarity 0.84Ulf P. Trociewitz et al. · 2011 · arXiv:1110.6814
Source status unknown — claims are unverified
Pulsed-field magnetization of drilled bulk high-temperature superconductors: flux front propagation in the volume and on the surface
similarity 0.83Gregory P Lousberg et al. · 2009 · arXiv:0908.1907
Source status unknown — claims are unverified
Dependence of Maximum Trappable Field on Superconducting Nb3Sn Cylinder Wall Thickness
similarity 0.83Mario Rabinowitz et al. · 2003 · arXiv:cond-mat/0308363
Source status unknown — claims are unverified