Electron- and hole-doping on ScH$_{2}$ and YH$_{2}$: Effects on superconductivity without applied pressure

S. Villa-Cortés, O. De la Peña-Seaman

arXiv:2106.10379 · DOI 10.1088/1361-648X/ac17ae · 2021-06-18 · Journal of Physics: Condensed Matter

T4experimental9 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We present the evolution of the structural, electronic, and lattice dynamical properties, as well as the electron-phonon coupling and superconducting critical temperature ($T_c$) of ScH$_2$ and YH$_2$ metal hydrides solid solutions, as a function of the electron- and hole-doping content. The study was performed within the density functional perturbation theory, taking into account the effect of zero-point energy through the quasi-harmonic approximation, and the solid solutions Sc$_{1-x}M_{x}$H$_{2}$ ($M$=Ca,Ti) and Y$_{1-x}M_{x}$H$_{2}$ ($M$=Sr,Zr) were modeled by the virtual crystal approximation. We have found that, under hole-doping ($M$=Ca,Sr), the ScH$_2$ and YH$_2$ hydrides do not improve their electron-phonon coupling properties, sensed by $λ(x)$. Instead, by electron-doping ($M$=Ti,Zr), the systems reach a critical content $x \approx 0.5$ where the latent coupling is triggered, increasing $λ$ as high as $70\%$, in comparison with its $λ(x=0)$ value. Our results show that $T_c$ quickly decreases as a function of $x$ on the hole-doping region, from $x=0.2$ to $x=0.9$, collapsing at the end. Alternatively, for electron-doping, $T_c$ first decreases steadily until $x=0.5$, reaching its minimum, but for $x > 0.5$ it increases rapidly, reaching its maximum value of the entire range at the Sc$_{0.05}$Ti$_{0.95}$H$_2$ and Y$_{0.2}$Zr$_{0.8}$H$_2$ solid solutions, demonstrating that electron-doping can improve the superconducting properties of pristine metal hydrides, in the absence of applied pressure.

Source-reported materials — not catalogue approval

FormulaReported Tc (K)Pressure (GPa)Type
Sc0.05Ti0.95H2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

3.7Pressure unresolvedunknown
Sc0.05Ti0.95H2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

1.9Pressure unresolvedunknown
Y0.2Zr0.8H2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

2.4Pressure unresolvedunknown
Y0.2Zr0.8H2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

1.2Pressure unresolvedunknown

Similar papers