Superconductivity at 44.4 K achieved by intercalating EMIM+ into FeSe
Jinhua Wang, Qing Li, Wei Xie, Guanyu Chen, Xiyu Zhu, Hai-Hu Wen
arXiv:2107.06017 · DOI 10.1088/1674-1056/ac1f09 · 2021-07-13 · Chinese Physics B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconductivity with transition temperature Tc above 40 K was observed in protonated FeSe (Hy-FeSe) previously with the ionic liquid of EMIM-BF4 used in the electrochemical process. However, the real superconducting phase is not clear until now, and detailed structural, magnetization and electrical transport measurements are lacking. By using similar protonating technique on FeSe single crystals, we obtained superconducting samples with Tc above 40 K. We show that the obtained superconducting phase is not Hy-FeSe but actually an organic-ion (C6H11N2+ referred to as EMIM+)-intercalated phase (EMIM)xFeSe. By using X-ray diffraction technique, two sets of index peaks corresponding with different c-axis lattice constants are detected in the protonated samples, which belong to the newly formed phase of intercalated (EMIM)xFeSe and the residual FeSe, respectively. The superconductivity of (EMIM)xFeSe with Tc of 44.4 K is confirmed by resistivity and magnetic susceptibility measurements. Temperature dependence of resistivity with different applied magnetic fields reveals that the upper critical field Hc2 is quite high, while the irreversibility field Hirr is suppressed quickly with increasing temperature till about 20 K. This indicates that the resultant compound has a high anisotropy with a large spacing between the FeSe layers.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| (C6H11N2)xFeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 44.4 | Pressure not reported | unknown |
Similar papers
Band structure of organic-ion-intercalated (EMIM)FeSe superconductor
similarity 0.92L. V. Begunovich & M. M. Korshunov · 2022 · arXiv:2201.00465
Source status unknown — claims are unverified
Superconducting phases in (NH3)yMxFeSe1−zTez (M=Li,Na,andCa)
similarity 0.92Yusuke Sakai et al.
Source status unknown — claims are unverified
Superconductivity in (NH3)yCs0.4FeSe
similarity 0.91Lu Zheng et al.
Source status unknown — claims are unverified
Emergence of magnetism and controlling factors of superconductivity in Li/Na-ammonia co-intercalated FeSe1-zTez
similarity 0.90Hechang Lei et al. · 2014 · arXiv:1406.3733
Source status unknown — claims are unverified
Enhanced superconductivity and anisotropy of FeTe0.6Se0.4 single crystals with Li-NH3 intercalation
similarity 0.90Chenghe Li et al. · 2017 · arXiv:1708.05310
Source status unknown — claims are unverified
Electrochemical synthesis and crystal structure of the organic ion intercalated superconductor (TMA)0.5Fe2Se2 with Tc = 43 K
similarity 0.90Bettina Rendenbach et al. · 2020 · arXiv:2012.01225
Source status unknown — claims are unverified