Enhancement of functional properties of V$_{0.6}$Ti$_{0.4}$ alloy superconductor by the addition of yttrium

SK. Ramjan; L. S. Sharath Chandra; Rashmi Singh; P. Ganesh; Archna Sagdeo; M. K. Chattopadhyay

doi:10.1063/5.0058170

← Back to search

Enhancement of functional properties of V$_{0.6}$Ti$_{0.4}$ alloy superconductor by the addition of yttrium

SK. Ramjan, L. S. Sharath Chandra, Rashmi Singh, P. Ganesh, Archna Sagdeo, M. K. Chattopadhyay

arXiv:2111.11670 · DOI 10.1063/5.0058170 · 2021-11-23

T1theoretical8 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We show here that the yttrium is immiscible and precipitates with various sizes in the body centred cubic V$_{0.6}$Ti$_{0.4}$ alloy superconductor. The number and size of the precipitates are found to depend on the amount of yttrium added. Precipitates with various sizes up to 30~$μ$m are found in the V$_{0.6}$Ti$_{0.4}$ alloy containing 5 at.\% yttrium. The large amount of line disorders generated by the addition of yttrium in this alloy are found to be effective in pinning the magnetic flux lines. While the superconducting transition temperature increases with the increasing amount of yttrium in the V$_{0.6}$Ti$_{0.4}$ alloy, the critical current density is maximum for the alloy containing 2 at. \% yttrium, where it is more than 7.5 times the parent alloy in fields higher than 1~T. We found that the effectiveness of each type of defect in pinning the flux lines is dependent on the temperature and the applied magnetic filed.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
V0.6Ti0.4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.68	Pressure not reported	midpoint
V0.6Ti0.4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.68	Pressure not reported	onset
V0.55Ti0.4Y0.05 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.85	Pressure not reported	midpoint
V0.55Ti0.4Y0.05 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.85	Pressure not reported	onset
V0.6Ti0.4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.68	Pressure not reported	unknown