Superconductivity of high-entropy-alloy-type transition-metal zirconide (Fe,Co,Ni,Cu,Ga)Zr2
Md. Riad Kasem, Hiroto Arima, Yoichi Ikeda, Aichi Yamashita, Yoshikazu Mizuguchi
arXiv:2207.06747 · DOI 10.1088/2515-7639/ac8e34 · 2022-07-14 · Journal of Physics: Materials
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We synthesized a new high-entropy-alloy-type (HEA-type) superconductor (Fe,Co,Ni,Cu,Ga)Zr2 with a Tc of 2.9 K. The EDX analyses revealed that the actual composition of the transition-metal site (Tr-site) is Tr = Fe0.18Co0.18Ni0.16Cu0.25Ga0.23, which gives the configurational entropy of mixing ΔSmix = 1.60R for the Tr site. Neutron powder diffraction revealed that the sample has a tetragonal CuAl2-type (space group: #140). The lattice constant of a monotonically decreases with decreasing temperature, but the lattice constant of c does not exhibit a clear shrinkage. Isotropic displacement parameter for both the Tr and Zr sites are large, which is probably caused by the HEA-type Tr site. The small temperature dependences of Uiso for both sites also indicate the presence of the local structural disorder in (Fe,Co,Ni,Cu,Ga)Zr2. From electrical resistivity, magnetic susceptibility, and specific heat measurements, bulk superconductivity was confirmed.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Fe0.18Co0.18Ni0.16Cu0.25Ga0.23Zr2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 2.9 | Pressure not reported | unknown |
| Fe0.18Co0.18Ni0.16Cu0.25Ga0.23Zr2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 2.9 | Pressure not reported | unknown |
| Fe0.18Co0.18Ni0.16Cu0.25Ga0.23Zr2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 2.9 | Pressure not reported | unknown |
Similar papers
Synthesis of high-entropy-alloy-type superconductors (Fe,Co,Ni,Rh,Ir)Zr2 with tunable transition temperature
similarity 0.95Md. Riad Kasem et al. · 2020 · arXiv:2011.05590
Source status unknown — claims are unverified
Superconductivity in HEA-type compounds
similarity 0.89Y. Mizuguchi & A. Yamashita · 2021 · arXiv:2102.01321
Source status unknown — claims are unverified
Superconductivity in equimolar Nb-Re-Hf-Zr-Ti high entropy alloy
similarity 0.89Sourav Marik et al. · 2018 · arXiv:1804.10092
Source status unknown — claims are unverified
Superconductivity and hardness of the equiatomic high-entropy alloy HfMoNbTiZr
similarity 0.86Jiro Kitagawa et al. · 2022 · arXiv:2207.11845
Source status unknown — claims are unverified
Superconductivity near the Mott-Ioffe-Regel limit in the high-entropy alloy superconductor (ScZrNb)(RhPd) with a CsCl-type lattice
similarity 0.86Sylwia Gutowska et al. · 2023 · arXiv:2308.03153
Source status unknown — claims are unverified
Superconducting ground state of nonsymmorphic superconducting compound ZrIr
similarity 0.86Manasi Mandal et al. · 2021 · arXiv:2106.00268
Source status unknown — claims are unverified