Hidden Granular Superconductivity Above 500K in off-the-shelf graphite materials

Raphael Rousset-Zenou; Samar Layek; Miguel Monteverde; Frédéric Gay; Didier Dufeu; Manuel Núñez-Regueiro

← Back to search

Hidden Granular Superconductivity Above 500K in off-the-shelf graphite materials

Raphael Rousset-Zenou, Samar Layek, Miguel Monteverde, Frédéric Gay, Didier Dufeu, Manuel Núñez-Regueiro

arXiv:2207.09149 · 2022-07-19

T4theoretical4 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

It has been reported that graphite hosts room temperature superconductivity. Here we provide new results that confirm these claims on different samples of highly oriented pyrolytic graphite (HOPG) and commercial flexible graphite gaskets (FGG). After subtraction of the intrinsic graphite diamagnetism, magnetization measurements show convoluted ferromagnetism and superconducting-like hysteresis loops. The ferromagnetism is deconvoluted by fitting with a sigmoidal function and subtracting it from the data. The obtained superconducting-like hysteresis loops are followed to the highest available temperature, 400K. The extrapolation of the decrease of its moment width with temperature indicates a transition temperature T$_{c}$$\sim$ 550K$\pm$50K for all samples. Electrical resistance measurements confirm the existence at these temperatures of a transition in HOPG samples, albeit without percolation. Besides, the FGG show transitions at temperatures (70K, 270K) near to those reported previously on intercalated-deintercalated graphite, confirming the general character of these superconducting transitions. These results are the first steps in the unveiling of the above room temperature superconductivity of graphite.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Hg Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.1	Pressure not reported	unknown
Nb3Ge Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	22.3	Pressure not reported	unknown
YBa2Cu3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	90	Pressure not reported	unknown
HgBa2Ca2Cu3O8+x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	166	26 GPa	unknown