Strong electron-phonon coupling and predicted highest known $T_{c}$ of MXenes revealed in 2H-Mo$_{2}$N under biaxial stress

Komsilp Kotmool; Prutthipong Tsuppayakorn-aek; Thiti Bovornratanaraks; Thanayut Kaewmaraya; Rachsak Sakdanuphab; Aparporn Sakulkalavek; Rajeev Ahuja; Wei Luo

doi:10.1016/j.physb.2024.416551

Strong electron-phonon coupling and predicted highest known $T_{c}$ of MXenes revealed in 2H-Mo$_{2}$N under biaxial stress

Komsilp Kotmool, Prutthipong Tsuppayakorn-aek, Thiti Bovornratanaraks, Thanayut Kaewmaraya, Rachsak Sakdanuphab, Aparporn Sakulkalavek, Rajeev Ahuja, Wei Luo

arXiv:2207.10863 · DOI 10.1016/j.physb.2024.416551 · 2022-07-22 · Physica B: Condensed Matter

T1experimental4 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

This letter reports the unexpectedly strong electron-phonon coupling (EPC) and the highest $T_c$ record ($\approx$ 38 K) among the MXenes revealed in the 2H-Mo$_2$N under biaxial stress. At first, its excellent mechanical properties are demonstrated with ideal strength of 37 GPa and elastic modulus of 438 GPa. Subsequently, EPC and corresponding $T_c$ are elucidated upon the dynamically stable range of strain. For strain-free 2H-Mo$_2$N, the EPC constant ($λ$) and $T_c$ are 1.3 and 22.7 K, respectively. This $T_c$ is higher than those of 2H-Mo$_2$C (4.3 K), 1T-Mo$_2$N (16.8 K), and other pristine MXenes. The material exhibits remarkable enhancement in $λ$ and $T_c$ when subject to compressive and tensile stresses. The obvious strong EPC with $λ$ over 2.0 occurs at strains of -4%, -2.5%, and 5%, yielding $T_c$s of 37.8, 35.4, and 28.9 K, respectively. Our findings suggest that the strain-dependent feature and energy levels of electronic bands play an essential role in enhancing EPC. Moreover, the stronger EPC in Mo$_2$N compared with Mo$_2$C is clarified based on lattice vibrations. Therefore, this work paves a practical way for designing 2D superconducting materials using tuning atomic recipes and strain-dependent engineering.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Mo2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	22.7	Pressure not reported	unknown
Mo2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37.8	Pressure not reported	unknown
Mo2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	35.4	Pressure not reported	unknown
Mo2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28.9	Pressure not reported	unknown
Mo2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.3	Pressure not reported	unknown
Mo2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16.8	Pressure not reported	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	39	Pressure not reported	unknown
NbSe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20	Pressure not reported	unknown
Mg2B4C2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	47	Pressure not reported	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	67	Pressure not reported	unknown
Mo2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mo2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.1	Pressure not reported	unknown
Mo2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.2	Pressure not reported	unknown
Mo2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16	Pressure not reported	unknown
W2N3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown