Synthesis and Superconductivity in Yttrium-Cerium Hydrides at Moderate Pressures

Liu-Cheng Chen; Tao Luo; Philip Dalladay-Simpson; Ge Huang; Zi-Yu Cao; Di Peng; Federico Aiace Gorelli; Guo-Hua Zhong; Hai-Qing Lin; Xiao-Jia Chen

Synthesis and Superconductivity in Yttrium-Cerium Hydrides at Moderate Pressures

Liu-Cheng Chen, Tao Luo, Philip Dalladay-Simpson, Ge Huang, Zi-Yu Cao, Di Peng, Federico Aiace Gorelli, Guo-Hua Zhong, Hai-Qing Lin, Xiao-Jia Chen

arXiv:2208.05191 · 2022-08-10

T2theoretical2 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Inspired by the high critical temperature in yttrium superhydride and the low stabilized pressure in superconducting cerium superhydride, we carry out four independent runs to synthesize yttrium-cerium alloy hydrides. The phases examined by the Raman scattering and x-ray diffraction measurements. The superconductivity is detected with the zero-resistance state at the critical temperature in the range of 97-140 K at pressures ranging from 114 GPa to 120$\pm$4 GPa. The maximum critical temperature of the synthesized hydrides is larger than those reported for cerium hydrides, while the corresponding stabilized pressure is much lower than those for superconducting yttrium hydrides. The structural analysis and theoretical calculations suggest that the phase of Y$_{0.5}$Ce$_{0.5}$H$_9$ has the space group $P6_3/mmc$ with the calculated critical temperature of 119 K, in fair agreement with the experiments. These results indicate that alloying superhydrides indeed can maintain relatively high critical temperature at modest pressures accessible by many laboratories.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Y0.5Ce0.5H9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	140	120 GPa	onset
Y0.5Ce0.5H9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	131	114 GPa	zero_resistance
Y0.5Ce0.5H9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	97	120 GPa	onset
Y0.5Ce0.5H9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	119	Pressure not reported	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	260	170 GPa	unknown
YH4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	88	155 GPa	unknown
YH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	220	180 GPa	unknown
YH9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	243	201 GPa	unknown
YH9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	262	182 GPa	unknown
CeH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	115	95 GPa	unknown
CeH9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	57	88 GPa	unknown