Phase Transitions and Superconductivity in Ternary Hydride Li$_2$SiH$_6$ at High Pressures

Sixuan Wu; Bin Li; Zhi Chen; Yu Hou; Yan Bai; Xiaofeng Hao; Yeqian Yang; Shengli Liu; Jie Cheng; Zhixiang Shi

doi:10.1063/5.0080880

← Back to search

Phase Transitions and Superconductivity in Ternary Hydride Li$_2$SiH$_6$ at High Pressures

Sixuan Wu, Bin Li, Zhi Chen, Yu Hou, Yan Bai, Xiaofeng Hao, Yeqian Yang, Shengli Liu, Jie Cheng, Zhixiang Shi

arXiv:2209.05014 · DOI 10.1063/5.0080880 · 2022-09-12 · Journal of Applied Physics

T3theoretical12 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We predicted a new ternary hydride Li$_2$SiH$_6$ at high pressures. A systematic structure search in Li$_2$SiH$_6$ compound reveals novel stable phases with intriguing electronic and phonon properties. It is found that Li$_2$SiH$_6$ is dynamically stable from ambient pressure up to 400 GPa with three novel phases: P312, P$\bar{3}$, and P$\bar{6}$2m. The calculation of electron-phonon coupling combined with Bardeen-Cooper-Schrieffer's argument indicates that this compound may be a candidate for high $T_c$ superconductors under high pressures. In particular, the maximum $T_c$ of $P\bar{6}2m$-Li$_2$SiH$_6$ at 400 GPa reaches 56 K. These findings may pave the way for obtaining room temperature superconductors in dense hydrogen-rich compounds.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Li2SiH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	56	400 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	203	Pressure not reported	unknown
Fe2SH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.3	173 GPa	unknown
YS4H4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20	200 GPa	unknown
YSH5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.7	300 GPa	unknown
BaReH9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure not reported	unknown
Li2MgH16 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	472	250 GPa	unknown
LiSi2H9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	54	172 GPa	unknown
LiSiH8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	77	250 GPa	unknown
LiPH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	150	200 GPa	unknown
Li2BH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	100	100 GPa	unknown