Superconductivity Induced by Site-Selective Arsenic Doping in Mo$_5$Si$_3$

Bin-Bin Ruan; Jun-Nan Sun; Meng-Hu Zhou; Qing-Song Yang; Ya-Dong Gu; Gen-Fu Chen; Lei Shan; Zhi-An Ren

doi:10.1021/acs.inorgchem.2c01647

← Back to search

Superconductivity Induced by Site-Selective Arsenic Doping in Mo$_5$Si$_3$

Bin-Bin Ruan, Jun-Nan Sun, Meng-Hu Zhou, Qing-Song Yang, Ya-Dong Gu, Gen-Fu Chen, Lei Shan, Zhi-An Ren

arXiv:2209.15231 · DOI 10.1021/acs.inorgchem.2c01647 · 2022-09-30 · Inorganic chemistry

T3experimental1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Arsenic doping in silicides has been much less studied compared with phosphorus. In this study, superconductivity is successfully induced by As doping in Mo$_5$Si$_3$. The superconducting transition temperature ($T_c$) reaches 7.7 K, which is higher than those in previously known W$_5$Si$_3$-type superconductors. Mo$_5$Si$_2$As is a type-II BCS superconductor with upper and lower critical fields of 6.65 T and 22.4 mT, respectively. In addition, As atoms are found to selectively take the 8$h$ sites in Mo$_5$Si$_2$As. The emergence of superconductivity is possibly due to the shift of Fermi level as a consequence of As doping, as revealed by the specific heat measurements and first-principles calculations. Our work provides not only another example of As doping, but also a practical strategy to achieve superconductivity in silicides through Fermi level engineering.