Nb-substitution suppresses the superconducting critical temperature of pressurized MoB$_2$

J. Lim; S. Sinha; A. C. Hire; J. S. Kim; P. M. Dee; R. S. Kumar; D. Popov; R. J. Hemley; R. G. Hennig; P. J. Hirschfeld; G. R. Stewart; J. J. Hamlin

doi:10.1103/PhysRevB.108.094501

Nb-substitution suppresses the superconducting critical temperature of pressurized MoB$_2$

J. Lim, S. Sinha, A. C. Hire, J. S. Kim, P. M. Dee, R. S. Kumar, D. Popov, R. J. Hemley, R. G. Hennig, P. J. Hirschfeld, G. R. Stewart, J. J. Hamlin

arXiv:2302.13936 · DOI 10.1103/PhysRevB.108.094501 · 2023-02-27 · Physical Review B

T1experimental1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

A recent work has demonstrated that MoB$_2$, transforming to the same structure as MgB$_2$ ($P6/mmm$), superconducts at temperatures above 30 K near 100 GPa [C. Pei $et$ $al$. Natl. Sci. Rev., nwad034 (2023)], and Nb-substitution in MoB$_2$ stabilizes the $P6/mmm$ structure down to ambient pressure [A. C. Hire $et$ $al$. Phys. Rev. B 106, 174515 (2022)]. The current work explores the high pressure superconducting behavior of Nb-substituted MoB$_2$ (Nb$_{0.25}$Mo$_{0.75}$B$_2$). High pressure x-ray diffraction measurements show that the sample remains in the ambient pressure $P6/mmm$ structure to at least 160 GPa. Electrical resistivity measurements demonstrate that from an ambient pressure $T_c$ of 8 K (confirmed by specific heat to be a bulk effect), the critical temperature is suppressed to 4 K at 50 GPa, before gradually rising to 5.5 K at 170 GPa. The critical temperature at high pressure is thus significantly lower than that found in MoB$_2$ under pressure (30 K), revealing that Nb-substitution results in a strong suppression of the superconducting critical temperature. Our calculations indeed find a reduced electron-phonon coupling in Nb$_{0.25}$Mo$_{0.75}$B$_2$, but do not account fully for the observed suppression, which may also arise from inhomogeneity and enhanced spin fluctuations.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Nb0.25Mo0.75B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure unresolved	unknown
Nb0.25Mo0.75B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4	50 GPa	unknown
Nb0.25Mo0.75B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5.5	170 GPa	unknown
Nb0.25Mo0.75B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	19.58	100 GPa	unknown
MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	32	110 GPa	unknown
MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	29.17	100 GPa	unknown
NbB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.86	Pressure unresolved	unknown
NbB2 Archive — disputed claim Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.62	Pressure not reported	unknown
NbB2 Archive — disputed claim Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9	Pressure not reported	unknown
NbB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure not reported	unknown
Mo0.95Sc0.05B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.8	Pressure not reported	unknown
Mo0.96Zr0.04B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5.9	Pressure not reported	unknown
Zr0.96V0.04B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.7	Pressure not reported	unknown
Zr0.96Nb0.04B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.1	Pressure not reported	unknown
Nb1-xB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.2	Pressure not reported	unknown
NbBx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.4	Pressure not reported	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	39	Pressure not reported	unknown
WB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	17	90 GPa	unknown