Superconducting Gap Structure of Filled Skutterudite LaOs$_4$As$_{12}$ Compound through $μ$SR Investigations

A. Bhattacharyya; D. T. Adroja; A. D. Hillier; P. K. Biswas

doi:10.3390/magnetochemistry9050117

← Back to search

Superconducting Gap Structure of Filled Skutterudite LaOs$_4$As$_{12}$ Compound through $μ$SR Investigations

A. Bhattacharyya, D. T. Adroja, A. D. Hillier, P. K. Biswas

arXiv:2307.03946 · DOI 10.3390/magnetochemistry9050117 · 2023-07-08 · Magnetochemistry

T1experimental1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Filled skutterudite compounds have gained attention recently as an innovative platforms for studying intriguing low-temperature superconducting properties. Regarding the symmetry of the superconducting gap, contradicting findings from several experiments have been made for LaRu$_{4}$As$_{12}$ and its isoelectronic counterpart, LaOs$_{4}$As$_{12}$. In this vein, we report comprehensive bulk and microscopic results on LaOs$_{4}$As$_{12}$ utilizing specific heat analysis and muon-spin rotation/relaxation ($μ$SR) measurements. Bulk superconductivity with $T_C$ = 3.2 K was confirmed by heat capacity. The superconducting ground state of the filled-skutterudite LaOs$_{4}$As$_{12}$ compound is found to have two key characteristics: superfluid density exhibits saturation type behavior at low temperature, which points to a fully gapped superconductivity with gap value of $2Δ/k_BT_C$ = 3.26; additionally, the superconducting state does not show any sign of spontaneous magnetic field, supporting the preservation of time-reversal symmetry. These results open the door for the development of La-based skutterudites as special probes for examining the interplay of single- and multiband superconductivity in classical electron-phonon systems.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaOs4As12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.2	Pressure not reported	midpoint
LaOs4As12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.2	Pressure not reported	unknown
LaOs4As12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
PrOs4Sb12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.8	Pressure not reported	unknown
PrRu4Sb12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.97	Pressure not reported	unknown
PrRu4As12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.4	Pressure not reported	unknown
LaFe4P12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.1	Pressure not reported	unknown
LaOs4P12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.8	Pressure not reported	unknown
LaRu4Sb12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.6	Pressure not reported	unknown
LaRu4As12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10.3	Pressure not reported	unknown
LaRu4As12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown