Semiconducting transport in Pb$_{10-x}$Cu$_x$(PO$_4$)$_6$O sintered from Pb$_2$SO$_5$ and Cu$_3$P

Li Liu; Ziang Meng; Xiaoning Wang; Hongyu Chen; Zhiyuan Duan; Xiaorong Zhou; Han Yan; Peixin Qin; Zhiqi Liu

doi:10.1002/adfm.202308938

← Back to search

Semiconducting transport in Pb$_{10-x}$Cu$_x$(PO$_4$)$_6$O sintered from Pb$_2$SO$_5$ and Cu$_3$P

Li Liu, Ziang Meng, Xiaoning Wang, Hongyu Chen, Zhiyuan Duan, Xiaorong Zhou, Han Yan, Peixin Qin, Zhiqi Liu

arXiv:2307.16802 · DOI 10.1002/adfm.202308938 · 2023-07-31 · Advanced Functional Materials

T3experimental29 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The very recent claim on the discovery of ambient-pressure room-temperature superconductivity in modified lead-apatite has immediately excited sensational attention in the entire society, which is fabricated by sintering lanarkite (Pb2SO5) and copper(I) phosphide (Cu$_3$P). To verify this exciting claim, we have successfully synthesized Pb$_2$SO$_5$, Cu$_3$P, and finally the modified lead-apatite Pb$_{10-x}$Cu$_x$(PO$_4$)$_6$O. Detailed electrical transport and magnetic properties of these compounds were systematically analyzed. It turns out that Pb$_2$SO$_5$ is a highly insulating diamagnet with a room-temperature resistivity of ~7.18x10$^9$ Ohm.cm and Cu$_3$P is a paramagnetic metal with a room-temperature resistivity of ~5.22x10$^{-4}$ Ohm.cm. In contrast to the claimed superconductivity, the resulting Pb$_{10-x}$Cu$_x$(PO$_4$)$_6$O compound sintered from Pb$_2$SO$_5$ and Cu$_3$P exhibits semiconductor-like transport behavior with a large room-temperature resistivity of ~1.94x10$^4$ Ohm.cm although our compound shows greatly consistent x-ray diffraction spectrum with the previously reported structure data. In addition, when a pressed Pb$_{10-x}$Cu$_x$(PO$_4$)$_6$O pellet is located on top of a commercial Nd$_2$Fe$_{14}$B magnet at room temperature, no repulsion could be felt and no magnetic levitation was observed either. These results imply that the claim of a room-temperature superconductor in modified lead-apatite may need more careful re-examination, especially for the electrical transport properties.