J. Y. Nie; X. F. Yang; X. Zhang; X. Q. Liu; W. Xia; D. Z. Dai; C. C. Zhao; C. P. Tu; X. M. Kong; X. B. Jin; Y. F. Guo; S. Y. Li

Pressure-induced double-dome superconductivity in kagome metal CsTi3Bi5

J. Y. Nie, X. F. Yang, X. Zhang, X. Q. Liu, W. Xia, D. Z. Dai, C. C. Zhao, C. P. Tu, X. M. Kong, X. B. Jin, Y. F. Guo, S. Y. Li

arXiv:2308.10129 · 2023-08-20

T2theoretical6 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We present high-pressure resistance measurements up to 40 GPa on recently discovered titanium-based kagome metal CsTi$_3$Bi$_5$. At ambient pressure, CsTi$_3$Bi$_5$ shows no evidence of superconductivity in resistivity and specific heat. By applying pressure, superconductivity emerges and the superconducting transition temperature ${\it T}_{\rm c}$ reaches its first maximum of 1.2 K at $\sim$5 GPa. Then the ${\it T}_{\rm c}$ is suppressed by pressure and cannot be detected around 10 GPa, manifesting as a superconducting dome. Remarkably, upon further increasing pressure above $\sim$13 GPa, another superconducting dome shows up, with the maximum ${\it T}_{\rm c}$ of 0.6 K and ending pressure at $\sim$36 GPa. The variation of ${\it T}_{\rm c}$ displays a clear double-dome shape in the superconducting phase diagram. Our work demonstrates the similarity between CsTi$_3$Bi$_5$ and CsV$_3$Sb$_5$, providing valuable insights into the rich physics of these novel kagome metals.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure unresolved	unknown
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure unresolved	unknown
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	0.9 GPa	onset
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.21	4.1 GPa	onset
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	12.7 GPa	onset
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.63	17.7 GPa	onset
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	36.5 GPa	onset
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.17	6.4 GPa	onset
CsTi3Bi5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	15.3 GPa	unknown
CsV3Sb5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2	2 GPa	unknown
CsBi2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.65	Pressure not reported	unknown