A possible explanation for the high superconducting Tc in bcc Ti at high pressure

Antonio Sanna; Camilla Pellegrini; Simone di Cataldo; Giannni Profeta; Lilia Boeri

← Back to search

A possible explanation for the high superconducting Tc in bcc Ti at high pressure

Antonio Sanna, Camilla Pellegrini, Simone di Cataldo, Giannni Profeta, Lilia Boeri

arXiv:2308.14672 · 2023-08-28

T5theoretical7 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Motivated by unexpected reports of a 26 K superconducting transition in elemental titanium at high pressure, we carry out an accurate ab-initio study of its properties to understand the rationale for this observation. The critical superconducting temperatures (Tc's) predicted under the assumption of a phononic pairing mechanism are found to be significantly lower than those experimentally observed. We argue that this disagreement cannot be explained by an unconventional coupling, as previously suggested, or by the existence of competing metastable structural phases. As a physically meaningful hypothesis to reconcile experimental and theoretical results, we assume the presence of Ti vacancies in the lattice. Our first-principles calculations indeed show that lattice vacancies can cause pressure dependent phonon softening and substantially increase the electron-phonon coupling at high pressure, yielding computed Tc's in agreement with the experimental measurements over the full pressure range from 150 to 300 GPa. We expect the proposed Tc enhancement mechanism to occur on a general basis in simple high-symmetry metals for various types of defects.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5	300 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	22.6	120 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20.6	150 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16.9	200 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.4	250 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.9	300 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26.7	150 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	24.4	200 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	25.2	250 GPa	unknown
Ti Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26.3	300 GPa	unknown